Ferrous Alloys

7 cases · 16 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Detail focus: Brittle Fracture clear all

Ferrous Alloys — sub-branches

Carbon Steel 18Cast Iron 8High Alloy Steel 27Low Alloy Steel 31Tool Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Fracture aspect of the casting cylinder at the 10.5 mm thickness, showing a brittle behavior (lack of plastic deformation). The internal side of the cylinder is to the top of the figure, and the painted surface is to the bottom of the figure.
129
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Aspect of the fracture surface of the 2" diameter casting. The fracture appeared flat, with secondary cracks, and the position of the fracture during the loading test is located in the region that was in tensile stress during the hot dip galvanized process (the part was sustaining its own weight during the zinc hot dip bath).
801
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Aspect of the fracture surface after cutting the valve body and opening the crack. The fracture is brittle.
55
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
The hose connector fracture surface presented different fracture micromechanisms associated to the microstructure: inclusion decohesion, small regions of intergranular fractures (probably due to cementite at grain boundaries), and cleavage of the ferritic structure. All these mechanisms are brittle.
560
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
Aspect of the housing after opening the through wall cracking. The fracture is brittle and presents chevron marks.
25
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Fracture Surface AspectDf - Brittle Fracture
Scanning electron fractography of a chromium plated pin, close to the pin surface where the fatigue cracking started, showing intergranular morphology typical of a hydrogen embrittlement effect. It occurred because the low alloy pin was carburized, quenched and tempered, with a too high hardness structure, before the electrolytic plating.
837
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The spring presents intergranular and transgranular brittle aspects in the fracture surface.
886
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Detailed aspect of the cylinder fracture, the internal surface to the top of the figure and the painted external surface to the bottom of the figure.
103
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture
Fractographic detail of the graphite decohesion and cleavage facets in the center of the cast cylinder thickness.
47
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Scanning electron fractography in low magnification (originally 15x), showing the flat fracture surface with steps and secondary cracks.
73
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
ML00103 — Brittle Fracture of a Free-Cutting ConnectorM - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Aspect of the internal side of the connector. The fracture, in the longitudinal direction, presents a brittle aspect. The thickness of the connector is about 2 mm.
126
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the brittle fracture, in the longitudinal direction.
105
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Details of the cleavage fracture in the ferritic structure.
86
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Fractography by SEMDf - Brittle Fracture
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
The low magnification fractography by SEM shows a brittle fracture of the spring wire, with several secondary cracks.
45
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fractography by SEM presents intergranular (in the previous austenite grain boundaries) and transgranular fracture micromechanisms. Several secondary cracks perpendicular to the fracture surface.
46
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture