Ferrous Alloys

9 cases · 16 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Kalling Etched Macro clear all

Ferrous Alloys — sub-branches

Carbon Steel 31Cast Iron 9High Alloy Steel 52Low Alloy Steel 56Tool Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
This macrography shows a longitudinal section of the tubular cast fitting. The external side is to the top and the internal side to the bottom. The buttering layer is evident in the groove that would be welded to the centrifugall cast tube (right side) and part of the ID and OD. During the buttering welding of the casting the cracks were not detected because they were formed in the center of the thickness and some have propagated to the internal diameter, but not to the external diameter. They opened only when the buttered casting was welded to the tube.
20
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Longitudinal Section
Macrography of the longidutinal section of a non broken allen bolt, at the threaded body to bolt head transition. The granular structure is different through the bolt, with refined structure in the threaded body and coarse at the transition.
44
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Longitudinal Section
17-4 PH rod, tubular, OD 10.6mm, wall thickness about 3.5 mm. Macrography of the rod in a transverse section showing the pitting in a position where it is almost through wall.
86
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched MacroDf - Pitting
Macrography of a longitudinal section of the fitting to tubing weld, with the longitudinal cracking at the tubular fitting position.
69
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Kalling Etched MacroDf - Longitudinal Section
Macrography of a longitudinal section of the broken bolt, at the fracture position, showing that the fracture is partially flat (left side), where the macroscopically aspect is brittle, and a final ductile fracture (right side). Interesting to note that there is a large longitudinal crack, secondary (transverse to the fracture surface).
143
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Longitudinal Section
Macrography of the welded joint upper part. Transverse section showing the different zones studied in this ML. See the schematic drawing in the next image.
454
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
Macrography of a transverse section of the welded joint between the original casting and the inserted casting, in the side of the original part.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched MacroDf - Fusion Line Left Side
Macrography of the NEW TUBE, centrifugally cast, in the transverse section, presenting columnar grains close to the external surface.
50
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section

More from these cases

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Macrographic detail close to the internal diameter (ID in the bottom), where the cracks were detected by dye check (after removal of the damaged part of the cast fitting). Close to the surface it is possible to see the layers of the weld metal that corresponds to the cast fitting buttering.
21
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Cracks
Welding Cracks in an Aged HP Cast Fitting
2
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Cracks
Welding Cracks in an Aged HP Cast Fitting
1
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Microhardness identations
ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Macrography of the fitting to tubing welded joint. The internal surface of the fitting (left side) is rough compared to the internal surface of the tubing (right side). The cracking is located only in the fitting and presented no association with the welded joint.
41
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Kalling Etched MacroDf - Longitudinal Section
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Macrography of the welded joint, at the root position, presenting the different zones studied in this ML. Transverse section. See the schematic drawing in the next image.
47
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Macrography of a transverse section of the welded joint between the original casting and the inserted casting, in the side of the inserted part.
17
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched MacroDf - Fusion Line Right Side
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Macrography of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting thickness loss and macrostructure deterioration.
33
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section