High Alloy Steel

3 cases · 55 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Welding clear all

High Alloy Steel — sub-branches

Martensitic Stainless Steel 1Nickel Alloy Steel 1Super Duplex Stainless Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the tubing fusion line. The welding was conducted in two passes. The average hardness at the heat affected zone of the tubing is 257 HV5.
825
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Left Side
The 8" ND, 1 1/4" thick, seamless pipe that was welded by GMAW process in 6G position. The testpiece was adopted for ASME IX qualification tests.
402
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Macrography of the welded joint upper part. Transverse section showing the different zones studied in this ML. See the schematic drawing in the next image.
454
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint

More from these cases

ML00100 — Superduplex Tubing to Forging Welded JointM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Micrography of the tubing heat affected zone.
69
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - HAZ Left Side
Micrography of the tubing heat affected zone.
68
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - HAZ Left Side
Macrography of the welded joint between a forging connector (right side) and a seamless tubing (left side). It was welded in two passes by GTAW process.
168
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Low magnification micrography of the superduplex stainless steel tubing (base metal), in the longitudinal direction. Refined ferritic-austenitic structure. The average hardness in the section is 264HV5.
58
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Base Metal Left Side
Micrography of the superduplex stainless steel tubing (base metal), in the longitudinal direction. Refined ferritic-austenitic structure.
55
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Duplex structure

+11 more from this case →

ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Transversal section of the 625 nickel alloy multipass weld. Pipe of 1 1/4' thickness
71
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
Schematic drawing presenting the transversal section of the 625 nickel alloy multipass weld
55
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Identification drawingDf - Welded Joint
Micrography of the base metal presenting a banded microstructure in the longitudinal section of the pipe.
51
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of a longitudinal section of the base metal presenting a quenched and tempered microstructure.
49
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the low temperature heat affected zone of the pipe. The intercritical temperature (IC) is evident in the decorated grain boundaries of the previous austenite.
42
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

+11 more from this case →

ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Schematic drawing presenting the different zones of the welded joint at the upper part.
49
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Identification drawingDf - Welded Joint
Macrography of the welded joint, at the root position, presenting the different zones studied in this ML. Transverse section. See the schematic drawing in the next image.
47
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
Schematic drawing presenting the different zones of the welded joint
35
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Identification drawingDf - Welded Joint
Base metal micrographic detail presenting a tempered martensitic microstructure.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrographic detail of the heat-affected zone close to the base metal.
29
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone

+15 more from this case →