Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Detail focus: Crack clear all

High Alloy Steel — sub-branches

Austenitic / Martensitic 1Austenitic Stainless Steel 16Duplex Stainless Steel 1Heat Resistant Steel 4High Mn Austenitic Steel 1Lean Duplex Stainless Steel 1Martensitic Stainless Steel 8Precipitation Hardened Stainless Steel 4Super Duplex Stainless Steel 5Wear Resistant Steel 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
24
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Crack
Transverse section of the 14" pipe in the center of the 2" branch using a weldolet fitting welded to the main pipe. The internal side of the pipe is to the top of the figure and the through wall fatigue cracking is located at the margem of the weld. It is possible to see that it is a full penetration weld and the fitting thickness is several times larger than the pipe thickness.
174
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Electrolytically Etched MacroDf - Crack
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
Detail of the fusion line region of the repair weld. Cracks filled with oxides indicating that the material was already corroded when the bead was deposited.
105
VIEW
ML00015 / Oct.2017
Intergranular Corrosion of 304SS Plate
M - Austenitic Stainless SteelP - Rolled PlateAp - RefineryCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Crack
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack
Aspect of the magnetic particle result in the sample cut from the blade. The yellow scale is in mm.
76
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Aspect Before AnalysisDf - Crack
Micrographic detail of the through wall cracking in the middle of the thickness, showing that the cracking is associated to ferrite network in the (super)duplex microstructure.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Micrography by SEMDf - Crack

More from these cases

ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Micrograph showing a fine acicular martensitic matrix with a branching crack network, more extensive near the right edge.
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
Micrography of a transverse section of the ring, in the center, where the cracking was closed. The cracks are intergranular and not opened to the surface.
29
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
ML00017 — Casting Defect in CA6NMM - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Linear indication in the sample, after metallographic preparation. The "cracking" is a casting defect.
65
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched MacroDf - Crack
ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Micrographic detail of the cracking, associated to the ferrite network, that presents both corrosion (preferential dissolution) and fracture (clevage) aspects.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Crack