Carbon Steel

3 cases · 21 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Automotive Capture method: Optical Microscope clear all

Carbon Steel — sub-branches

Low Carbon Steel 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography as polished of the longitudinal section of the bolt at the fracture position. The fracture (top of the figure) is rough, characteristic of a ductile fracture.
196
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - As polished micrographyDf - Fracture
Micrography of the ferritic low carbon steel plate (8 mm superior plate).
80
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the longitudinal section of the ring, showing a fully ferritic structure.
619
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00120 — Ductile Rupture of a Carbon Steel Eye BoltM - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Micrography of a longitudinal section of the bolt in the center of the thickness, presenting a ferritic pearlitic structure with elongated grains due to the forming process, without later heat treatment.
173
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic pearlitic structure, with grains sligthly elongated.
157
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the bolt at the bottom of the thread fillet, presenting a plastically deformed ferritic pearlitic structure in a very small extension from the surface (about 0.1mm). This analysis was conducted in a position far from the failure and the structure was created by the cold forming process to manufacture the thread.
152
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Rolled Thread
Micrographic detail of a longitudinal section of the bolt at the bottom of the thread fillet, presenting a plastically deformed ferritic pearlitic structure. This analysis was conducted far from the failure and the structure was created by the cold forming process to manufacture the thread.
147
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Micrography of a longitudinal section of the bolt at the thread fillet adjacent to the fracture, presenting a ductile cracking from the bottom of the fillet, propagating with a strong plastic deformation. The deformation lines of the cold formed process (thread cold rolling) are also deformed by the cracking propagation.
141
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - Nital Etched Micrography by OMDf - Ductile Crack

+1 more from this case →

ML00069 — Liquation Cracks in SAW of Low Carbon SteelM - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Micrographic detail of the ferritic low carbon steel plate (8 mm superior plate).
80
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrographic detail of the weld metal presenting a typical low carbon steel structure (acicular ferrite and previous austenite grain boundary ferrite).
78
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal presenting a typical low carbon steel structure (acicular ferrite and previous austenite grain boundary ferrite).
72
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the fracture at the superior plate (8 mm thickness). The fracture occurred in the coarse grain heat affected zone.
60
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography of the fracture at the fillet weld margin. The fracture occurred in the coarse grain heat affected zone of the superior plate (8 mm thickness).
54
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fracture

+3 more from this case →

ML00057 — Low Carbon Steel of Segment RingM - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Longitudinal section of the ring, showing a fully ferritic structure.
128
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the ring reveals a very fine ferritic structure.
115
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
93
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section
Transverse section of the ring presenting a fully ferritic structure, that presents a hardness level a little higher probably due to a cold forming effect.
54
VIEW
ML00057 / Apr.2017
Low Carbon Steel of Segment Ring
M - Low Carbon SteelP - Machined PartAp - AutomotiveCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Transverse Section