Sampling and Analysis

10 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Transverse Section Aspect clear all

Sampling and Analysis — sub-branches

General View 4Transverse Section 9Weld Metal 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail of the IWRC with 6 strands of 7 wires plus the core. It is possible to see that the outer wires of the external strands are plastically deformed, mainly in the upper side of the figure; and the core is manufactured using galvanized wires.
39
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - General View
Aspect of the 3/8" thickness, 50 mm x 50 mm, 6061 T6 aluminum plate, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
23
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and cracks that appear in the opposite site of the plate at the projectile impact position.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the low carbon steel, in a section transverse to the impact position that is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet.
53
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Transverse Section AspectDf - Transverse Section
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the AR500 wear resistant steel, in a section transverse to the impact position evidencing lack of plastic deformation, or any other damage. The impact surface is to the top of the figure.
29
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
77
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Wire rope, nominal diamater 2". The wire includes an independent core (IWRC) with 7 wires of 2.0 mm and 6 strands with 26 wires (1+5+[5+5]+10). The external strand layer presents a 3.8mm wire, and there are two internal strand layers with different wire sizes. The wire rope presents plastic reinforcement. It is a right regular lay AACI made by extra improved plow steel (EIPS) wires.
876
VIEW
ML00117 / Jan.2018
High Carbon Steel Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Typical manufacturing
Cm - Transverse Section AspectDf - General View
Schematic drawing from a macrosection of the TR57 rail, showing the dimensions and usual terminology.
43
VIEW
ML00091 / Sep.2017
Flat Bottom Rail TR57
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Transverse Section AspectDf - General View

More from these cases

ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Detail of the IWRC with 6 strands of 7 wires plus the core. It is possible to see that the outer wires of the external strands are plastically deformed, mainly in the upper side of the figure; and the core is manufactured using galvanized wires.
3
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - General View
ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Aspect of the 3/8" thickness plate, 50 mm x 50 mm, of the titanium alloy, in a section transverse to the impact position that is to the top of the figure. The projectile did not perforate the plate but caused a localized plastic deformation and a shear effect.
15
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Transverse Section AspectDf - Transverse Section
ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Detail of the transverse section of the 4" pipe 90° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
70
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section
Detail of the transverse section of the 4" pipe 180° from the seam weld. The thickness of the pipe is 8 mm. No evidences of general corrosion or pitting were identified.
64
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Transverse Section