Sampling and Analysis

3 cases · 18 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Seamless Pipe Standard: API Capture method: Optical Microscope clear all

Sampling and Analysis — sub-branches

Base Metal 3Heat Affected Zone 1Longitudinal Section 3Transverse Section 4Weld Metal 4Welded Joint 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the pipe base metal, in a longitudinal section, presenting a slight banding and a refined structure.
147
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
13Cr SS longitudinal section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
437
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrography of the pipe base metal, in a longitudinal section. The ferritic structure is refined and it is possible to identify a small variation in the ferritic grain size, that is promoting the slight banding effect.
119
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the weded joint at the cap pass fusion line. The columnar structure of the weld metal is to the top of the figure; and it is possible to see the coarse grains at the heat affected zone. Both columnar structure and coarse grains are related to the previous austenite grain boundaries. From the fusion line to the base metal (in the bottom of the figure) the grain sizes are refined.
86
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography presenting the coarse grain heat affected zone of the welded joint, at the cap pass. The microstructure is bainitic.
82
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the weld metal in the region of the cap pass that was not reheated, last bead, presenting previous austenite columnar grains, coarse.
69
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography of the weld metal in the root, reheated by the fill pass, presenting a refined ferritic structure.
49
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint

+1 more from this case →

ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Micrography of a longitudinal section of the pipe substrate showing a uniform bainitic microstructure obtained by the pipe quenching and tempering,
72
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Low magnification micrography of a longitudinal section of the pipe at the interface between overlay layers, with electrolytic etch that reveals the Ni alloy structure, large columnar grains with celular morphology.
66
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
Micrography of a longitudinal section of the pipe at the interface between overlay layers, with electrolytic etch that reveals the Ni alloy structure, large grains with celular dendritic morphology.
52
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
Micrographic detail of a longitudinal section of the pipe in the overlay weld metal, with electrolytic etch that reveals the Ni alloy structure with celular dendritic morphology and precipitates.
49
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Chromic Acid Electrolytic EtchedDf - Weld Metal
ML00039 — Collapse in Tubular 13CrM - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
13Cr SS in the longitudinal section, at the collapsed region. Non uniform structure (ferritic matrix and decorated prior austenite grain boundaries) that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
54
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
13Cr SS in the transverse section, at the collapsed region, showing a non uniform structure that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
13Cr SS transverse section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
The micrography of the 13Cr SS in the transverse section, far from the collapsed region, shows a uniform tempered martensitic structure.
27
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
The micrography of the 13Cr SS in the transverse section, far from the collapsed region, shows a uniform tempered martensitic structure.
26
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section