Sampling and Analysis

7 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Bainite Capture method: Aspect Before Analysis clear all

Sampling and Analysis — sub-branches

External Surface 1General View 4Internal Surface 1Welded Joint 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the tube internal surface after removal from the boiler, presenting multiple longitudinal cracks.
295
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
96
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 4 1/2" nominal diameter seamless pipe internally overlaid with Alloy 625. This pipe corresponds to a 90° curve. The overlaid pipe was heat treated before and after bending. The final quenching and tempering heat treatment was conducted to meet API 5L X70 properties.
113
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Shaft pinion presenting the bearing surface, with machining markes, from where the thermal spray layer was detached. The diameter of the 880 mm long shaft in this region is about 75 mm.
426
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - General View
Aspect of the superheater ND 1" tube that was in operation for about 35,000 hours and presented a thick deposit at the external surface.
211
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Aspect Before AnalysisDf - General View
Aspect of three pins that were operating in a hydraulic system. Adjacent to the fracture of the broken pin (the one that is in the right side of the figure) it is possible to see multiple surface craks and detachment of the surface chromium layer.
88
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
The connector was welded to the pipe from both (internal and external) sides, a PWHT was applied and the part was machined. The UT indication was detected during final inspection.
78
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Aspect of the external surface of the leaking tube, after removal of the membrane.
262
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - External Surface