Sampling and Analysis

17 cases · 23 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Capture method: Aspect Before Analysis clear all

Sampling and Analysis — sub-branches

External Surface 4General View 18Internal Surface 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the broken stud that was fastening a flanged line in a subsea body (tapped hole) using a nut. The fracture, transverse to the stud axis, occurred exactly at the body to flange interface. Adjacent to the fracture, all thread fillets (positioned inside the flange hole) presented cracks at the bottom of the thread. The stud was operating during seven years and was not corroded, indicating it was protected by the anodes. There are also deposits in the fillets suggesting the cathodic protection was effective even inside the flange hole.
799
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Image of the external surface of the valve body at the region where the Alloy 625 insert was fillet weld to the SDSS valve body. The surface was later machined, so it is possible to see only a mark indicating where the weld is. The brittle crack is arrested at the margin of the weld. It is possible to see strong deformation at the crack tip when it arrives the weld.
41
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the broken bolt, 5/8" Allen, socket head cap screw, originally 1 3/4" long, broken in subsea service under cathodic protection. The bolt presents a zinc coating.
116
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Flanged case, 640mm long. The photo presents a general view of the instrumentation system, destroyed after only 6 months in subsea service. The system was manufactured using only 316 stainless steel and the case was 20 mm thick.
335
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - General View
Aspect of the Nitronic 60 cylinder, OD 36.4mm, presenting pits at the external surface.
219
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the bolt analyzed to qualify the lot of fasteners to be adopted in subsea conditions, exposed to cathodic protection.
62
VIEW
ML00106 / Dec.2017
Inconel 718 Submarine Bolt
M - NiCrFe AlloyP - BoltAp - SubseaCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Aspect of the bolt with a special head, to be adopted in subsea condition. M12, 1/2" 13UNC.
342
VIEW
ML00105 / Jun.2018
Inconel 718 Bolt of Special Head
M - NiCrFe AlloyP - FastenerAp - SubseaCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Aspect of the bolts M12 x 25.
41
VIEW
ML00101 / Nov.2017
High Strength 316SS Bolt
M - Austenitic Stainless SteelP - BoltAp - SubseaCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Aspect of the fracture of a small Allen bolt, nominal diameter 5/8" 1 3/4" long, class 12.9, that was operating in subsea environment during 5 years. The fracture is rusted but the thread still presents the zinc coating.
81
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Aspect of the instrument system after disassembling. The internal part of the case, where the electronic device was operating, was wet by seawater and failed to send signals to the surface.
258
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - General View
ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Aspect of the 17-4 PH rod, OD 10.6 mm, presenting deep pits at the external surface.
125
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - External Surface