Heat Affected Zone

3 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Martensite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the heat affected zone at the face of the joint. It is possible to see that even close to the fusion line the material was reheated in high temperature, suggesting that the temper bead was effective.
53
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Low magnification micrography of a longitudinal section of a 4 mm diameter wire, at the region where the pearlitic strain hardened wire is affected by the welding. The base metal is to the left side and the region of the HAZ that starts with a grain growth is to the right side.
24
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of a section transverse to the Oxygen Plasma Cut surface, showing the zone affected by the heat generated in the cutting. The extension of the HAZ is about 0.5 mm. The cut was conducted in the 1 1/4" thickness of the plate.
359
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

More from these cases

ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the heat affected zone at the face of the joint, close to the fusion line. The hardness level at the HAZ was 248 HV10.
58
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the root of the joint, submitted to several welding reheating cycles.
36
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat affected zone at the root of the joint, submitted to several welding reheating cycles. The structure is still martensitic but presented a refined previous austenite structure.
30
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
ML00113 — Autogenous Weld of a Carbon Steel WireM - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Micrography of a longitudinal section of a 4 mm diameter wire, at the heat affected zone created by the autogenous welding, presenting a tempered martensitic structure.
19
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Macrography of a transverse section of the cut surface showing the heat affected zone region.
29
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - NItal Etched MacroDf - Heat Affected Zone
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
32
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
27
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
27
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by SEMDf - Heat Affected Zone
Location of the microhardness tests. The three measurements at the plate base metal showed average hardness of 204 HV 50g. The three measurements of the martensitic structure at the surface showed average 454HV 50g. The intercritical region showed average 324 HV 50g.
25
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone