Damage

96 cases · 259 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Brittle Behavior 12Corrosion 39Ductile Behavior 5Fabrication Defect 20Fatigue 12High Temperature 9Hydrogen 17Lack of Sealing 1Repair Defect 1Shooting Effect 4Wear 3

Results

SortNewestOldestTitle A-ZTitle Z-A
The general aspect of the 1 1/8" 2H nut, presenting rejectable indications that appear like cracks, located in the face and in the lateral side of the nut.
46
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken padeye. The outer diameter is about 10" and the thickness of the casting is about 2".
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Drilling tool that broke close to the region of the male connector (pin end). The fracture is at the right side of the figure.
102
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the equipment presenting a through wall cracking at the margin of the fillet weld.
142
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Aspect of the hydraulic line samples removed from service to be analyzed. Tubing and welded joint (bottom sample) between the 316 tubing (left side of the sample) and the nitronic fitting (right side of the sample). The cracking is located 10 mm far from the weld, autogenous orbital GTAW.
108
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
Aspect of the fitting welded to a tubing, ND 5/8" in a hydraulic line. The through wall cracking is longitudinal in the fitting side.
1032
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - General View
The tool housing ID 1 1/2" presented a longitudinal through wall cracking, in two positions at 180°. The internal side of the housing presented several pits.
66
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Aspect of the inner side of a valve body, showing regions of localized corrosion and rust, not expected for this stainless steel.
82
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Corrosion

More from these cases

ML00099 — Forging Defect in a Cadmium Plated NutM - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Aspect in detail of the 1 1/8" 2H nut face, presenting rejectable indications that appear like cracks.
49
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap
The general aspect of the lateral side of the 1 1/8" 2H nut, presenting a rejectable indication that looks like a straight crack.
48
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap
ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
The fracture was removed from the failed part and analyzed separately. The aspect of the fracture surface is presented. It is flat, with regions of fatigue propagation and with regions of erosion by washout (to the right side of the figure).
80
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Detail of the fracture surface presenting a fatigue propagation from the outside of the tool.
69
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Detail of the fracture surface presenting erosion by a washout, because the equipment was pressurized when the cracking became through wall.
63
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Washout
ML00095 — MIC of a Riser Control LineM - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Detail of the welded joint between the 316 tubing (left side) and the nitronic fitting (right side). The through wall cracking is transverse to the line, in the fitting, 10 mm far from the weld, where the fitting was slightly bent to be assembled (cold bent).
65
VIEW
ML00095 / Sep.2017
MIC of a Riser Control Line
M - Austenitic Stainless SteelP - Fabrication WeldAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Welded Joint
ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Detail of the longitudinal through wall cracking in the fitting welded to a tubing, ND 5/8" in a hydraulic line.
87
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - External Surface
Aspect of the internal side of the fitting to tubing welded joint, after longitudinal cut. It is possible to see that the cracking (still filled with corrosion products) is located in the fitting side (left side) far from the welded joint to the tubing (right side).
58
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Internal Surface
ML00093 — MIC of a Drilling ToolM - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Aspect of the internal side of the housing presenting multiple cracks in longitudinal direction.
49
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Cracking
The aspect of the internal side of the housing showing pitting corrosion.
39
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Corrosion
Aspect of the internal side of the housing in detail, showing deposits, rust and pitting. There are some cracks inside pits.
37
VIEW
ML00093 / Sep.2017
MIC of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Heat Treated PartAp - O&G Well DrillingCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Pitting
ML00092 — MIC of a Valve BodyM - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Evidences of a stagnated fluid in the internal surface of the valve body.
61
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Internal Surface
Deep localized corrosion spots, rusted. There are indications that the roughness of the surface influences the localized corrosion location.
61
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Localized Corrosion