Damage

1 case · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Duplex Ferritic Austenitic Capture method: As polished micrography clear all

Damage — sub-branches

Brittle Behavior 1Corrosion 2Ductile Behavior 1Fabrication Defect 1Fatigue 1Lack of Sealing 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the sleeve, in a region where the two layers applied by thermal spray are sound, not detached. The grey layer (200 micros) is the tugnsten carbide; and the white layer (1000 microns) is a stainless steel. The substrate is white in the bottom of the figure.
24
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Thermal Spray Layer

More from these cases

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Micrography of a longitudinal section of the sleeve, in a region where the surface layer starts detachment. This grey layer is the tugnsten carbide; and the white layer (1000 microns) is a stainless steel. In this case the first TS layer is sound. The substrate is white in the bottom of the figure.
20
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Layer Detachment
Micrography of a longitudinal section of the sleeve, in a region where the surface layer was completely removed. In this position only the stainless steel layer is at the surface. That is why the sealing condition was lost. The substrate is white in the bottom of the figure.
19
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Layer Detachment
Micrographic detail of a longitudinal section of the sleeve, in a region where the WC (tungsten carbibe) surface layer was degradated and partially removed.
17
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Layer Detachment
Micrographic detail of the WC (tungsten carbibe) surface layer, degradated and partially removed.
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Layer Detachment
Micrography of a longitudinal section of the sleeve, in a region where the surface layer was completely removed. In this position only the stainless steel layer, that is porous and full of oxides, is at the surface. That is why the sealing condition was lost.
17
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - As polished micrographyDf - Thermal Spray Layer

+1 more from this case →