Scanning Electron Microscope

7 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Pipe clear all

Scanning Electron Microscope — sub-branches

Electrolytic Etch Micrography by SEM 3Fractography by SEM 8Micrography by SEM 5Nital Etched Micrography by SEM 2Surface Aspect by SEM 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal in the last bead, presenting previous austenite columnar grains, primary ferrite in the grain boundaries, some regions of ferrite with aligned second phases and acicular ferrite.
58
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by SEMDf - Weld Metal
Micrography of the seam welded joint, autogenous. The localized dissolution occurrs exactly at the weld metal that presents a bainitic structure and Vickers (100g) microhardness values about 230HV, compared to the heat affected zone presenting average of 202 HV and the base metal presenting average of 180HV.
59
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by SEMDf - Welded Joint
Image by scanning electron microscopy of the metallurgically bonded interface of the internally cladded pipe. It is a seamless pipe in a low alloy steel X70 cladded by welding overlay of Alloy 625 (by automatic GTAW process). The region is a detail of the interface inside the Ni alloy weld metal, presenting columnar grains and intragranular preciptation. The pipe was heat treated before bending (solution annealing) and after bending (quenching and tempering to meet X70 grade). The microhardness of this region is higher than the value obtained out of this region, in the overlay.
657
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Aspect of a micrographic sample by scanning electron microscopy showing the external pipe surface, in the bottom, the fracture at the left side of the figure and several spots of pitting corrosion from the external surface. The polished section (transverse to the fracture and in a longitudinal section of the pipe) shows the morphology of the pit , 0.2 mm depth. Original magnification 50x.
54
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by SEMDf - Pitting
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Aspect of the internal surface of the pipe at the welded region, showing the interface of the thinning area in the weld and the pipe base metal.
128
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Surface Aspect by SEMDf - Localized Thinning
Image of the external surface of the pipe presenting regions of localized corrosion (in the beginning) and deposits
387
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Micrography at the scanning electron microscopy showing the deposits inside the crevice. The microanalysis by EDS revealed the presence of Fe, O, as well as Cl and S.
35
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Micrography by SEMDf - Corrosion
ML00132 — Seamless Pipe Overlaid with Alloy 625M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Image by scanning electron microscopy of the interface of the internally cladded pipe. It is a seamless pipe in low alloy steel X70 overlaid with Alloy 625 (by automatic GTAW process). The region is a detail in the side of the Ni alloy weld metal, presenting transgranular precipitation. The pipe was heat treated before bending (solution annelaing) and after bending (quenching and tempering to meet X70 grade). The microhardness of this region is higher than the value obtained out of this region, in the overlay.
43
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Image by scanning electron microscopy of the interface of the internally cladded pipe, seamless low alloy steel X70 overlaid with Alloy 625 (by automatic GTAW process) and presenting maximum iron content of 5% at the thickness of 3 mm (the qualified thickness).
37
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Fracture aspect after opening the cracking, in the location where the fatigue cracking was iniciated. There is a pitting corrosion, 0.3 mm depth.
58
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Crack
Detail of the fatigue fracture iniciation point, at the surface, in a pitting corrosion 0.3 mm depth.
58
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Pitting
Fractographic detail of the pitting corrosion in the region of iniciation of the fatigue cracking, at the external surface of the pipe.
52
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Pitting
Detail of the fatigue fracture propagation, with striation micromechanism.
48
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fractographic detail of fatigue striation.
41
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+2 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Region of the localized thinning at the weld metal, in a metallographic section, as polished. In the base metal the hydride layer is continuous and no thinning is evident (left side of the figure) and in the weld metal it is detached and cracked (right side of the figure).
107
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Localized Thinning
Hydride layer at the internal surface of the pipe base metal, after Kroll etch.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Hydride Formation
Detail of the hydride layer at the internal surface of the pipe base metal, after Kroll etch.
62
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Hydride Formation
ML00014 — Pitting Corrosion in 316SS PipeM - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Image of the external surface of the pipe presenting deposits where there is a localized corrosion at the surface.
326
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion
Image of the external surface of the pipe presenting the aspect of the localized corrosion by pitting.
297
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Pitting