As polished micrography

6 cases · 25 images for “fatigue”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
The internal side of the tube presented multiple cracks, filled with oxides, blunt-tipped, typical of a corrosion fatigue cracking mechanism.
160
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Parallel cracks
The micrography of the longitudinal section of the tube, close to OD, shows the paralel cracks, filled with oxides, perpendicular to the surface.
1441
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Close to the External Surface
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
51
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - External Surface
Micrography in low magnification, as polished, of the crack in the the repair weld metal, showing the dendritic aspect of the hot cracks, formed during welding due to the high content of impurities in a high strength weld metal.
26
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrography of a typical as polished overloaded wire, in a longitudinal section, showing necking at the fracture and secondary ductile cracks. About 25% of the wires have ruptured by this ductile mechanism.
35
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polished micrographyDf - Ductile Fracture

More from these cases

ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrographic detail of the corrosion cracking from internal side of the tube, in several points at the tube surface.
156
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Corrosion Cracking
Corrosion Fatigue of a Boiler Waterwall Tube
4
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - As polished micrographyDf - Crack
ML00104 — Thermal Fatigue of a Boiler TubeM - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
The micrography of the longitudinal section of the tube, close to ID, shows the paralel cracks, filled with oxides, perpendicular to the surface.
229
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
115
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrographic details of the longitudinal section of the tube, close to OD, showing paralel cracks, filled with oxides, perpendicular to the surface.
109
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
103
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Cracks Transverse to the Surface
Micrographic details of the longitudinal section of the tube, close to ID, showing paralel cracks, filled with oxides, perpendicular to the surface.
99
VIEW
ML00104 / Dec.2017
Thermal Fatigue of a Boiler Tube
M - Low Carbon SteelP - Autogenously Welded TubeAp - BoilerCd - Thermal Fatigue
Cm - As polished micrographyDf - Thermal Fatigue Cracks
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
43
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - External Surface
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
Drill Pipe Fracture in the Pipe Body
3
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography, as polished, of the hot cracks with rounded morphology.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrographic detail, as polished, of the hot cracks with rounded interdenritic morphology.
26
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrography in low magnification, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
24
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Micrography, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
22
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Micrographic detail of the straight crack that propagated by a fatigue mechanism.
18
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack

+2 more from this case →

ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Branching, web-like network of corrosion attack penetrating along grain boundaries through the matrix.
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polished micrographyDf - Austenite