Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Aged Martensite Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The fractographic aspect of the broken bolt shows intergranular micromechanism, typical of a hydrogen embrittlement condition for this aged martensitic material.
88
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture
Corroded spots (shallow pits full of products) at the spring surface.
80
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Corrosion
Nitronic 60 cylinder. Scanning electron microscopy image of a corroded region at the external surface of the cylinder, that is austenitic. The image shows the localized corroded regions in form of pits.
1228
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion
Fractographic aspect of the broken fastener, at the surface, showing na intergranular morphology typical of a hydrogen assisted mechanism of a high strenght steel under cathodic protection.
224
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
The spring presents intergranular and transgranular brittle aspects in the fracture surface.
884
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture

More from these cases

ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Fractographic aspect by scanning electron microscopy, close to the surface the broken bolt, presenting intergranular fracture micromechanism.
79
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture
Microscopic detail of the intergranular fracture close to the bolt surface.
71
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture
Fractographic aspect by scanning electron microscopy, in the center of the broken bolt, presenting transgranular fracture micromechanism.
45
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Cleavage Facets
Fractographic detail of the transgranular fracture micromechanism, brittle.
43
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Cleavage Facets
ML00137 — Brittle Fracture of a 15-5 PH Valve SpringM - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Corroded spots (shallow pits full of products) at the spring surface.
75
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Surface Aspect by SEMDf - Corrosion
The scanning electron microscopy image presents the surface of the spring (top of the figure) where it was broken (the fracture is in the bottom of the figure). It is possible to see that there is a product at the surface and the material presents intergranular fracture, suggesting there was a hydrogen embrittlement effect. Important to observe that the material does not present pits.
58
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Fractography by SEMDf - At the Surface
The scanning electron microscopy image presents the fracture surface at the fracture initiation point. The fracture is intergranular.
54
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
Image detail presenting the intergranular fracture surface at the fracture initiation point.
46
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Fractography by SEMDf - Intergranular Fracture
Fracture micromechanism changing from intergranular to transgranular, as the fracture is propagating.
45
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Fractography by SEMDf - Fracture

+4 more from this case →

ML00121 — Pitting Corrosion in a Subsea SystemM - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Nitronic 60 cylinder. Scanning electron microscopy image of a corroded region at the external surface of the cylinder, that is austenitic. The image shows the structure revealed by dissolution of the material (inside the pits) evidencing the strain hardened layer that is presented at the cylinder surface due to the manufacturing process.
106
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion
Nitronic 60 cylinder. Scanning electron microscopy image detail of a corroded region inside a pitting showing the etched structure (strain hardened austenitic structure).
103
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion
Nitronic 60 cylinder. Scanning electron microscopy image of a corroded region in a pit, at the external surface of the cylinder. The corrosion (dissolution) revealed the strain hardened layer at the surface.
96
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Localized Corrosion
17-4 PH rod. Surface aspect by scanning electron microscopy showing a region where the passivation layer was destroyed and a pitting was in the begining.
86
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Pitting
ML00074 — Hydrogen Cracking of a 17-4 PH Subsea BoltM - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Microscopic aspect of the fracture, close to the bolt surface where the fracture is macroscopically brittle, presenting a predominantly intergranular fracture micromechanism.
108
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Microscopic aspect of the fracture, in the center of the bolt, presenting partial intergranular fracture micromechanism and partial quase cleavage mechanism.
98
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Microscopic aspect of the fracture, close to the bolt surface where the fracture is macroscopically ductile (probably the final fracture), presenting dimples as the fracture micromechanism.
89
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Ductile Fracture
ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
The low magnification fractography by SEM shows a brittle fracture of the spring wire, with several secondary cracks.
45
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fractography by SEM presents intergranular (in the previous austenite grain boundaries) and transgranular fracture micromechanisms. Several secondary cracks perpendicular to the fracture surface.
46
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture