4 cases · 23 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Ferritic matrix Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of CAP A, showing graphite in imperfect nodules and ferritic matrix.
481
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Imperfect Nodules
The cast iron microstructure is predominatly ferritic with graphite nodules.
169
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
The micrography of a longitudinal section of the pipe, close to the internal surface, shows a general corrosion mechanism (with slow wall thickness loss), although the graphite/matrix interface is corroded preferentially.
569
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Corrosion
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
632
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides

More from these cases

ML00047 — Ductile Cast Iron Caps of Electrical InsulatorsM - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Detail of CAP A microstructure. Graphite in imperfect nodules and ferritic matrix. Grey sulphide inclusions.
90
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP B, showing graphite in nodules and ferritic matrix.
67
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP B microstructure. Graphite in nodules and ferritic matrix. Small sulphide inclusions (grey).
60
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of CAP C, showing graphite in nodules and ferritic-perlitic matrix.
52
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Graphite in Nodules
Detail of CAP C microstructure. Graphite in nodules and ferritic-perlitic matrix.
56
VIEW
ML00047 / Mar.2017
Ductile Cast Iron Caps of Electrical Insulators
M - Ductile Cast IronP - Cast iron capAp - EnergyCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00034 — 45 Years Old Acquaduct Grey Cast IronM - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Micrographic detail of the graphite/matrix interface corrosion, leading to a general corrosion loss.
189
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Graphite in Flakes
Micrography of the longitudinal section of the pipe, close to the internal surface, showing graphite in flakes and ferritic matrix with small regions of perlite.
231
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic Matrix
Micrography of the longitudinal section of the pipe, close to the internal surface, showing graphite in flakes and ferritic matrix with small regions of perlite and eutetic in the middle of the perlite colonies.
192
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic Matrix
Micrography of the longitudinal section of the pipe, in the center of the thickness. Graphite in flakes and ferritic matrix with small regions of perlite.
179
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic Matrix
Micrography of the longitudinal section of the pipe, in the center of the thickness. Graphite in flakes and ferritic matrix with small regions of perlite.
162
VIEW
ML00034 / Apr.2017
45 Years Old Acquaduct Grey Cast Iron
M - Gray Cast ironP - Centrifugally Cast PipeAp - AcquaductCd - General Corrosion
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+4 more from this case →

ML00003 — Cast iron Engine Valve SeatsM - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
206
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
182
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
137
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure