Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: High Temperature Capture method: Optical Microscope Detail focus: Microstructure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the granular copper structure, a little far from the overheated region.
102
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Granular structure
Detailed microstructure of the plate base metal, exposed to high temperature exhausting gases. Refined austenite, precipitation of carbides in the grain boumdaries and some cracks.
23
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
SAMPLE 1 AT THE FRACTURE - Micrography at the position where the thickness is reduced to zero. Side A to the bottom. The microstructure is austenite with intergranular and transgranular precipitation. The position of the zero thickness presents aspect of an intergranular fracture, and in side A there are several intergranular cracks from the surface.
83
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Austenitic with Secondary Precipitation
Micrographic detail of the longitudinal section of the tube, close to the external surface. The carburizing layer consists of a bainitic structure, with intergranular and intragranular carbide precipitation.
1184
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
Micrography of the new tube close to a region of a casting defect (shrinkage), presenting only austenitic structure with a network of primary precipitates.
351
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Micrography of the transverse section of the NEW TUBE, in the center of the thickness, showing the austenitic structure with primary carbides network.
410
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Austenitic with Primary Carbides
Micrographic detail of a longitudinal section of the bolt far from the fracture, presenting a tempered structure.
82
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Tempered Structure
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
632
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Micrographic detail of the granular copper structure, out of the damaged area. The dark particles are non metallic (oxides).
93
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Granular structure
Micrographic aspect of the tube wall under the localized thinning, in a transverse section, showing a coarse structure due to high temperature grain growth.
37
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Overheating
Micrographic detail of the high temperature grain growth in the tube microstructure.
31
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Coarse Structure
Micrographic detail of the high temperature grain growth in the tube microstructure.
35
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Coarse Structure
Micrography of the interface between the melted steel (top) and the copper tube (bottom), showing a mixture of melted materials.
31
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Nital Etched Micrography by OMDf - Mixture of Melted Metals

+4 more from this case →

ML00174 — Carburization of a 347 SS Welded JointM - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Detailed microstructure of the weld metal, exposed to high temperature exhausting gases. Austeno-ferritic structure and some cracks.
21
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Ferrite and Austenite
Microstructure of the heat affected zone (weld metal to the left side), exposed to high temperature exhausting gases. Large austenitic grain size and intergranular cracks fully opened and filled with oxides.
21
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Oxalic Acid Electrolytic EtchDf - Coarse Structure
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 1 AT 1 mm THICKNESS - Micrography in the center of the thickness. The microstructure is austenitic with secondary precipitation, intergranular and intragranular.
76
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Austenitic with Secondary Precipitation
SAMPLE 1 AT 1 mm THICKNESS - Micrographic detail of the austenite with secondary precipitation. This oxalic acid electrolytic etch is revealing the integranular and transgranular (or intragranular) precipitation. In the grain boundaries it is possible to see: 1) a continuous network of carbide precipitation and 2) isolated islands of sigma phase. In the middle of the grains there are rounded and neddles like carbides.
72
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Austenitic with Secondary Precipitation
SAMPLE 2 AT 2 mm THICKNESS - Micrography in the center of the thickness. The microstructure is austenitic with secondary precipitation, intergranular and intragranular. There are no variations in the microstructure comparing to sample 1.
48
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Secondary Precipitation
SAMPLE 2 AT 2 mm THICKNESS - Micrographic detail of the austenite with secondary precipitation. This oxalic acid electrolytic etch is revealing the integranular and transgranular (or intragranular) precipitation. In the grain boundaries it is possible to see: 1) a continuous network of carbide precipitation and 2) isolated islands of sigma phase. In the middle of the grains there are rounded and neddles like carbides. There are no variations in the microstructure comparing to sample 1.
43
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Intergranular Precipitation
SAMPLE 3 AT 4 mm THICKNESS - Micrography in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation, but this micrography was obtained in the longitudinal section, presenting the plate alignment and was etched with NaOH, adopted to colour the sigma phase.
45
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - NaOH Electrolytic Etched MicroDf - Austenitic with Secondary Precipitation

+4 more from this case →

ML00107 — Carburized 9Cr1MoV Superheater TubeM - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Micrography of the longitudinal section of the tube, close to the internal surface. A thick scale is evident, but no microstructural changes compared to the center of the tube.
183
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
156
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
137
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of a longitudinal section of the tube in the center of the thickness, showing a ferritic-bainitic structure of this CrMoV steel.
142
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Bainite
Micrography of the longitudinal section of the tube, close to the external surface. A scale is evident at the surface as well as a carburizing layer.
549
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Nital Etched Micrography by OMDf - Carburized Layer
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Micrography of the tube removed from service after 6 month, close to a region of a casting defect (shrinkage), presenting austenitic structure with a network of primary precipitates (initial stage of coarsening) and intragranular secondary precipitation.
48
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Micrography of the transverse section of the TUBE REMOVED FROM SERVICE, in the center of the thickness, showing the austenitic structure with primary carbides network and secondary precipitation.
59
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Glyceregia Etched Micrography by OMDf - Intragranular Secondary Precipitation
ML00004 — Creep in High Temperature BoltsM - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Micrographic detail of a longitudinal section of the bolt close to the fracture, presenting an overtempered structure.
76
VIEW
ML00004 / Jun.2018
Creep in High Temperature Bolts
M - CrMo SteelP - FastenerAp - Gas TurbineCd - Creep
Cm - Nital Etched Micrography by OMDf - Overtempered Structure
ML00003 — Cast iron Engine Valve SeatsM - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
The intake valve seat cylinder, manufactured in a high alloy white cast iron, presents a network of primary carbides, not degradated even after high temperature exposition during all lifetime.
206
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Network of Primary Carbides
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
182
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure
The exhaust valve seat cylinder, manufactured in a high alloy white cast iron, presents a coalesced structure, degradated by high temperature exposition during the lifetime.
137
VIEW
ML00003 / Apr.2017
Cast iron Engine Valve Seats
M - White Cast IronP - Valve SeatAp - MaritimeCd - Microstructural Evolution
Cm - Micrography by OMDf - Coalesced structure