Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Finished Product Condition: Fabrication Defect Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the barrel nut that is broken in a brittle way (without plastic deformation). The Nut diameter is 1", the nut length is 2" and the bolt thread is 1/2" (nominal diameter).
753
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - General View
Aspect of the external surface of the broken cylindrical roller bearing presenting a polished external diameter and a the rupture with brittle characteristics (flat and parts that were lost).
726
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
Shaft pinion presenting the bearing surface, with machining markes, from where the thermal spray layer was detached. The diameter of the 880 mm long shaft in this region is about 75 mm.
426
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - General View
The general aspect of the 1 1/8" 2H nut, presenting rejectable indications that appear like cracks, located in the face and in the lateral side of the nut.
46
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Visual aspect of both sides of the fractures. They present a macroscopically brittle aspect, with chevron marks indicating the starting point at the thinner edge of the thread.
81
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
ML00131 — Brittle Failure of a Soft Roller BearingM - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Aspect of the broken cylindrical roller bearing, presenting the internal diameter full of cracks; and the fracture revealing two different morphologies, flat and smooth close to the external diameter (that appeared white in the macrography); and rough close to the internal diameter (that appeared dark in the macrography).
107
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
Aspect of the internal diameter surface presenting several cracks in the axial direction, caused by the contact with the shaft. The roller bearing presented a too low hardness level (21 HRc average) in this ID position.
90
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Internal Surface
ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Detail of the detached layer, about 1.5 mm thick.
48
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - Layer Detachment
ML00099 — Forging Defect in a Cadmium Plated NutM - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Aspect in detail of the 1 1/8" 2H nut face, presenting rejectable indications that appear like cracks.
49
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap
The general aspect of the lateral side of the 1 1/8" 2H nut, presenting a rejectable indication that looks like a straight crack.
48
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Aspect Before AnalysisDf - Lap