Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Transportation clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a wheel section close to the tread, where the material receives a localized surface hardening by quenching and tempering. The average hardness at the surface is 346HB and in the center is 196HB. The wheel was in operation for a long time and the analyzed part is at the wheel tread.
902
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - NItal Etched MacroDf - Transverse Section
Micrographic detail of a transverse section of the rail, in the head, showing a fully perlitic structure.
520
VIEW
ML00096 / Oct.2017
Carbon Steel Tee Rail
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrographic detail of the transverse section of the rail, in the head, showing a fully perlitic structure.
374
VIEW
ML00091 / Sep.2017
Flat Bottom Rail TR57
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Pearlite

More from these cases

ML00158 — Surface Hardened Carbon Steel WheelM - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Micrography of the wheel in the center of the thickness. The material presents a coarse structure.
88
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - In the Center of the Thickness
Micrography of the wheel in the center of the thickness, presenting a predominantly pearlitic structure and average hardness abot 196HB.
74
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the coarse pearlitic structure in the center of the wheel thickness. The part presents a wrought structure.
73
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrography of the wheel at the surface that was quenched and tempered. The material presents a tempered martensitic structure, with hardness that varied from 327HB to 363HB.
55
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface
Micrography of the wheel at the hardened surface, presenting a refined martensitic structure, tempered for average hardness of 346 HB.
50
VIEW
ML00158 / Feb.2020
Surface Hardened Carbon Steel Wheel
M - High Carbon SteelP - WheelAp - TransportationCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - At the Surface

+5 more from this case →

ML00096 — Carbon Steel Tee RailM - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Micrographic detail of a transverse section of the rail, in the head, showing a fully perlitic structure.
57
VIEW
ML00096 / Oct.2017
Carbon Steel Tee Rail
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Perlite
Micrography of a transverse section of the rail, in the head, showing equiaxial grains. Perlitic microstructure.
54
VIEW
ML00096 / Oct.2017
Carbon Steel Tee Rail
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Transverse Section
ML00091 — Flat Bottom Rail TR57M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Micrographic detail of the transverse section of the rail, in the head, showing a fully perlitic structure.
42
VIEW
ML00091 / Sep.2017
Flat Bottom Rail TR57
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Perlite
Micrography of a transverse section of the rail, in the head, showing equiaxial grains. Fully perlitic structure.
35
VIEW
ML00091 / Sep.2017
Flat Bottom Rail TR57
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Transverse Section
Schematic drawing from a macrosection of the TR57 rail, showing the dimensions and usual terminology.
42
VIEW
ML00091 / Sep.2017
Flat Bottom Rail TR57
M - High Strength Low AlloyP - RailAp - TransportationCd - Typical manufacturing
Cm - Transverse Section AspectDf - General View