Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Maritime Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Scanning electron microscopy of the internal surface of the tube, showing that under the deposits there are regions of localized corrosion.
30
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Internal Surface
Micrographic detail of the intergranular secondary cracks, parallel to the fracture, typical of a hydrogen assisted cracking. Close to the cracking it is possible to see an elongated inclusion, probably of a sulfide type.
26
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Micrography by SEMDf - Intergranular Cracking

More from these cases

ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Microscopic detail, by scanning electron microscope, of a region where there is a localized dissolution at the internal surface of the tube. The deposits are adhered at the surface and under the deposits, the analysis indicated increased sulfur levels, suggesting SRB (sulfate reduced bacteria) effects.
31
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Pitting
Scanning electron microscopy aspect of the region inside of a pit. The aspect is of a chemical attack, generated by the metabolic by-products of the adhered microorganism. The effect is of a localized dissolution and the granular tube microsctruture is revealed.
40
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface Aspect by SEMDf - Corrosion