Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Engine Standard: AISI Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the tubing showing a granular structure, austenitic.
52
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrography of the thermal spray (TS) layer showing the different alloys, gray oxides and black voids. The Ni base TS alloy is of a yellow colour at the interface with the shaft substrate (in the left). The Cr base TS alloy appears white, similar to the shaft substrate. Longitudinal section of the shaft.
42
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrography of a transverse section of the engine bearing, close to the internal surface, showing two layers of bearing alloys that presents a total thickness of 600 microns.
29
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Surface Layer

More from these cases

ML00167 — Fatigue of a Flared Tubing ConnectionM - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Micrography of a longitudinal section of the tubing, showing the austenitic structure free from strain hardening and free from grain boundary carbides.
51
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrographic detail of the austenitic structure, free from strain hardening and free from grain boundary carbides.
54
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrography of a longitudinal section of the tubing where the fracture occurred. the left side is the outer diameter and the right side is the inner diameter.
37
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - At the Surface
Micrography of a longitudinal section of the flared tubing where the fracture occurred. The starting point of the fracture is associated to the external side of the tubing, where it was connected by a nut and there was a localized plastic deformation due to the fitting assembly.
33
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Transgranular Fracture
Micrographic detail of the localized plastic deformation due to the fitting assembly, in the region where the fatigue has started.
30
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Plastic Deformation
ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Micrographic detail, as polished in a longitudinal section, of the interface between the shaft substrate and the thermal spray layer. In the left it is the shaft substrate also presenting parts of aligned inclusions (gray). In the center it is the Ni base TS alloy and in the right it is the Cr base TS alloy. There are also black voids and grey oxides.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrography of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
32
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Micrographic detail of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and (over) tempered structure. Longitudinal section.
35
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer
Shaft microstructure in the longitudinal section, showing aligned segregations typical of the material forming.
31
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

+4 more from this case →

ML00083 — Steel Back of a Bimetallic Engine BearingM - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Micrographic detail of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
26
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Predominantly Ferritic
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Micrography of a transverse section of the back steel of an engine bearing, presenting a predominantly ferritic structure, strain hardened.
24
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Strain Hardened