Tube

3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Fusion Line clear all

Tube — sub-branches

Autogenously Welded Tube 2Longitudinally Seam Welded 1Seamless Round Shape 4Seamless tube 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the external tube surface, presenting the cracking at the margin of the weld. This cracking could have been created by thermal induced cycles (fatigue), but it did not propagate into the tube wall.
85
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrography of the tubing fusion line. The welding was conducted in two passes. The average hardness at the heat affected zone of the tubing is 257 HV5.
825
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Left Side
Micrography of the low carbon steel plate at the fusion line, presenting a bainitic structure at the HAZ and ferritic structure in the weld metal.
82
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line

More from these cases

ML00100 — Superduplex Tubing to Forging Welded JointM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Micrography of the forging fusion line. The welding was conducted in two passes. The average hardness of the heat affected zone is 273 HV5.
39
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Fusion Line Right Side