Wire Rope

2 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrosection of the wire rope, transverse, showing 6 strands and an independent wire rope core (IWRC). Each strand presents three layers in a SEALE construction.
92
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - Plastic Deformation
General aspect of the degradated wires of the strand, most part presenting rust and rupture. There are two mais aspects of the degradation: wire thickness reduction by corrosion and cracks creating a longitudinal fracture of several wires.
96
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Metallographic detail of the wire surface in one strand external wire, showing the presence of oxides.
39
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Oxide Layer
Detail of the cracks associated to deformed regions in the outer wire of a strand.
40
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - Cracks
One disassembled wire, 3.2mm diameter, from a strand. The wire presents strong plastic deformation. In a very localized area.
29
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - Plastic Deformation
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Macrography of a typical corroded wire in a longitudinal section, showing loss of thickness by corrosion.
75
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Corrosion
Macrography of one wire that was fully cracked, in a longitudial section. The morphology shows multiple corrosion-fatigue cracking.
62
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Multiple cracks
Macrography of one wire that was overloaded, showing localized necking and large plastic deformation close to the fracture. This kind of fracture occurred for about 25% of the broken wires.
50
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Ductile Fracture
Micrography of a typical corroded wire, in a longitudinal section, showing loss of thickness by corrosion. The microstructure of the wire is predominantly pearlitic and the wire presents no coating, in any region.
54
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrography of a typical corroded wire, in a longitudinal section as polished, showing loss of thickness by corrosion. The loss of material is accelerated by the corrosion in "layers" associated to the strained microstructure.
43
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - As polishedDf - Corrosion

+14 more from this case →