Microstructure

Pick a branch below to see matching micrographs

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Search & filters

Search

42 images

TryUNS ML00091 corrosion AISI ML00015 brittle fracture Finished Product ductile behavior Raw Material fatigue Damage hydrogen Corrosion fracture embrittlement stress corrosion

Sharpest next filters

UNS
Sampling and Analysis
Corrosion
Low Alloy Medium Carbon QT
Raw Material

Browse by category (5)

Standard37

UNS8 cases
AISI6 cases
API6 cases
5D5 cases
ASTM5 cases
S1355 cases
A4 cases
41303 cases

+29 more

G413003 cases
43402 cases
Colmonoy 52 cases
Commercial Name2 cases
Modified2 cases
1821 case
4330V1 case
4491 case
4791 case
481 case
5931 case
5L1 case
898-11 case
ALLOY1 case
class 8.81 case
F1 case
F117011 case
G863001 case
grade 251 case
grade F221 case
grade S327501 case
grade X651 case
group 7 Alloy 630 AH1 case
ISO1 case
P5501 case
S174001 case
S327501 case
S43100 mod1 case
Type 11 case

Product21

Finished Product15 cases
Raw Material14 cases
Drill Pipe5 cases
Tubular Forging5 cases
Forged Pin3 cases
Forging3 cases
Heat Treated Part2 cases
Pipe2 cases

+13 more

Allen Bolt1 case
Body1 case
Bolt1 case
Casting1 case
Drill Collar1 case
Fabrication Weld1 case
Fastener1 case
Longitudinal Seam Welded Pipe1 case
Machined Part1 case
Pin1 case
Seamless Pipe1 case
Valve Body1 case
Welded Joint1 case

Condition18

Damage16 cases
Corrosion6 cases
Corrosion Fatigue4 cases
Fabrication Defect3 cases
Hydrogen3 cases
Hydrogen Embrittlement3 cases
Sound3 cases
Ductile Behavior2 cases

+10 more

Fatigue2 cases
Typical manufacturing2 cases
Welding Defect2 cases
Bending1 case
Brittle Behavior1 case
Fatigue Induced by a Defect1 case
Heat Treatment Defect1 case
Mechanical Fatigue1 case
Pitting Corrosion1 case
Thermal spray1 case

Material11

Ferrous Alloys19 cases
Low Alloy Steel14 cases
Low Alloy Medium Carbon QT13 cases
High Alloy Steel4 cases
Cast Iron1 case
CrMo Steel1 case
Gray Cast iron1 case
High Mn Austenitic Steel1 case

+3 more

Martensitic Stainless Steel1 case
Precipitation Hardened Stainless Steel1 case
Super Duplex Stainless Steel1 case

Detail focus19

Damage25 images
Sampling and Analysis17 images
General View11 images
Fracture9 images
Brittle Fracture3 images
Corrosion3 images
At the Surface2 images
Fatigue Fracture2 images

+11 more

Internal Surface2 images
Crack1 image
Cracking1 image
External Surface1 image
Layer Detachment1 image
Localized Corrosion1 image
Longitudinal Section1 image
Multiple cracks1 image
Pitting1 image
Through Wall Cracking1 image
Washout1 image

Atlas / Microstructure

Application: O&G Well Drilling ×Capture method: Aspect Before Analysis ×clear all

Browse Microstructure

Aged Martensite 1 Austenite 1 Bainite 1 Coating Layer 1 Columnar Grains 1 Duplex Ferritic Austenitic 1 Ferritic Bainitic 1 Ferritic pearlitic 1 Granular 1 Graphite in flakes 1 Large Grains 1 Martensite 3 Martensite and Retained Austenite 2 Pearlitic Matrix 1 Refined ferritic 1 Segregation Bands 3 Strain Hardened 1 Surface layer of Thermal Spray 2 Tempered Martensite 11