Titanium Alloy

5 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Microstructure clear all

Titanium Alloy — sub-branches

Ti6Al4V 3Unalloyed Titanium 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Granular alpha structure of the pipe base metal.
49
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Alpha
Micrography of the plate in the middle of the thickness, showing the aligned structure tyical of a rolling process. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
The microstructure of the pipe base metal, in the center of the thickness, is granular alpha.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Granular structure
The plate longitudinal section presents a granular refined structure. Biphasic.
340
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Grain refined structure
The bar presented a large prior beta grain size and acicular alpha. Biphasic structure.
420
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Coarse Structure

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography showing the alpha plus beta microstructure in the middle of the thickness. The sample was mechanically-electrolitically polished and etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
32
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the alpha (light grains as a matrix) plus beta (dark phase) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
28
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta phase (dark) in the alpha grains (light) microstructure. Etched with HF (10%) + HNO3 (5%) +H2O (85%) solution.
24
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrographic detail of the plate, showing the aligned beta (dark phase) in alpha microstructure. Etched with HF+ HNO3+H2O solution.
26
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta
Micrography by SEM of the plate in the middle of the thickness, showing the alpha microstructure (dark grains) and the beta phase (light). Etched with HF+HNO3+H2O.
35
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Alpha and Beta

+2 more from this case →

ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
The microstructure of the pipe seam weld metal, in the center of the thickness, presents a coarse prior beta grain size.
85
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Columnar Grains
ML00029 — Titanium Plate for Subsea ApplicationM - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Alpha and beta phases. Refined Structure.
52
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Alpha and beta phases. Refined Structure.
46
VIEW
ML00029 / Jan.2017
Titanium Plate for Subsea Application
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
ML00028 — Titanium Bar for Subsea ApplicationM - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
The bar presented alpha plus beta phases, acicular alpha and coarse prior beta grains.
97
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Two phases
Acicular alpha structure in a biphasic alloy of a large prior beta grain size. 4" diameter bar.
100
VIEW
ML00028 / Jan.2017
Titanium Bar for Subsea Application
M - Ti6Al4VP - BarAp - StructureCd - Typical manufacturing
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Acicular Alpha