Ferrous Alloys

20 cases · 32 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Transverse Section Aspect clear all

Ferrous Alloys — sub-branches

Carbon Steel 31Cast Iron 9High Alloy Steel 52Low Alloy Steel 56Tool Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
The macrography of a longitudinal section of the shell plate (sample removed from the boiler), at the position of the fillet weld (sealing weld) with a tube, where surface welding repairs created conditions for cracking the base material in a transgranular morphology. Several cracks were identify starting from the steam drum internal surface.
448
VIEW
ML00019 / Apr.2017
Transgranular SCC in Boiler Steam Drum
M - CMn SteelP - Rolled PlateAp - BoilerCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks
A small sample containing cracks was removed from the cracked weld metal, by mechanical means.
81
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Transverse Section AspectDf - Weld Metal
The macrography of a transverse section of the shell to flange weld (Lepto's etch) shows that the cracking occurred through the shell plate thickness, at the margin of the fillet weld.
93
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Transverse Section AspectDf - Cracking
Transverse section of the 2" diameter pipe at the pitting location. The pipe was leaking.
1323
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Transverse Section AspectDf - Pitting