View of the fracture. The internal green coating was removed only close to the fracture.
29
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Fracture Surface AspectDf - Fracture
Fracture appearance of one side of the broken part showing chevron marks coming from the thinner part of the fracture. The socket thickness is only 13 mm at this point.
77
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
After cutting the pipe and opening the crack, the fracture appearance shows a clean fracture, flat, starting from the margem of the weld of the pipe (right side of the figure), and propagating through wall into the pipe (aproximately 5 mm thickness). The external side of the pipe is to the right side of the figure (presenting the weld finishing) and the internal side of the pipe is to the left side of the figure.
176
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - Fracture Surface AspectDf - Fracture
The fracture is flat, in the region of the lower resistant section, presenting no macroscopic evidences of plastic deformation. The starting point of the fracture is indicated by the chevron marks.
62
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
Aspect of the bolt fracture, presenting a flat surface.
80
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Aspect of the fracture surface after cutting the valve body and opening the crack. The fracture is brittle.
55
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macroscopic aspect of the fracture surface, showing a brittle behavior (chevron marks) and a starting point at the bottom of the groove in the right side of the figure.
42
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fracture Surface AspectDf - Brittle Fracture
Macroscopic detail of the fracture surface with a starting point at the external surface of the pin.
82
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Fracture appearance of the other side of the broken part, also evidencing chevron marks coming from the thinner part of the fracture.
63
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed macroscopic aspect of the chevron marks in the fracture, starting at the internal surface of the socket, in a region in contact with the bolt that was being torked. The thickness socket is 13 mm at this point.
54
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Chevron Marks
Detailed macroscopic aspect of the chevron marks in the other side of the fracture, starting at the internal surface of the socket, in a region in contact with the bolt that was being torked. The thickness socket is 13mm at this point.
51
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Chevron Marks
ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Macroscopically brittle fracture of the barrel nut, starting at the edge of the thread, as shown by the chevron marks.
29
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
The fracture, that occurred at the region of transition between the threaded body and the bolt head, presented a flat and brittle aspect.
69
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
ML00080 — MIC of Stacking Disc SpringsM - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Detail of the fracture starting point, in the bottom of the groove, where there is a pit about 0.5 mm depth.
36
VIEW
ML00080 / Sep.2017
MIC of Stacking Disc Springs
M - Low Alloy Medium Carbon QTP - SpringAp - SubseaCd - Brittle Behavior
Cm - Fracture Surface AspectDf - Brittle Fracture