Low Alloy Steel

1 case · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 4820 clear all

Low Alloy Steel — sub-branches

High Strength Low Alloy 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Shaft pinion presenting the bearing surface, with machining markes, from where the thermal spray layer was detached. The diameter of the 880 mm long shaft in this region is about 75 mm.
426
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Detail of the detached layer, about 1.5 mm thick.
48
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - Layer Detachment
Macrographic detail of the thermal spray layer in a position of the shaft where it was not detached. Longitudinal section of the shaft. The waves are the machining marks created to anchor the thermal spray layer, that is about 1.5mm thick.
41
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - NItal Etched MacroDf - Longitudinal Section
Micrography of the thermal spray (TS) layer showing the different alloys, gray oxides and black voids. The Ni base TS alloy is of a yellow colour at the interface with the shaft substrate (in the left). The Cr base TS alloy appears white, similar to the shaft substrate. Longitudinal section of the shaft.
42
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrographic detail, as polished in a longitudinal section, of the interface between the shaft substrate and the thermal spray layer. In the left it is the shaft substrate also presenting parts of aligned inclusions (gray). In the center it is the Ni base TS alloy and in the right it is the Cr base TS alloy. There are also black voids and grey oxides.
33
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - As polished micrographyDf - Coating Layer
Micrography of the interface between the shaft surface and the thermal spray layer. The shaft steel presents a quenched and tempered structure. Longitudinal section.
32
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Coating Layer

+7 more from this case →