Low Alloy Steel

12 cases · 50 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: As polished micrography clear all

Low Alloy Steel — sub-branches

CMn Steel 13CrMo Steel 4High Strength Low Alloy 7Low Alloy Low Carbon QT 2Low Alloy Medium Carbon QT 23Low Alloy Wear Resistant 1Low Alloy for Thermochemical Treatment 2Microalloyed Steel 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the spring, at the surface, indicating that there are multiple intergranular cracks initiating from the pit.
26
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Multiple cracks
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - External Surface
Micrography in low magnification, as polished, of the crack in the the repair weld metal, showing the dendritic aspect of the hot cracks, formed during welding due to the high content of impurities in a high strength weld metal.
26
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrography of the plate section, as polished, close to the surface that suffered the impact. No evidences of damage.
26
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrography of the cracking parallel to the fracture, as polished. The fracture is branched, there are several secondary cracks, with a clear intergranular morphology.
65
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Cracking
As polished micrography of the bottom of the thread fillet, where a cracking is still closed, showing the microscopical morphology of the cracking.
39
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracking
Micrography of the longitudinal section of the stud showing internal cracks, secondary (not the cracks that opened the fracture). It is evident that the cracking from the thread fillet, of a ductile aspect, presented a different aspect than the internal cracks, of a brittle aspect.
31
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, in the "as polished" condition, showing the zinc flakes coating layer, applied by a painting process that do not create metallurgical bonding with the substrate.
82
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer

More from these cases

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Micrographic aspect of the multiple intergranular cracks, initiating from the bottom of a pit.
25
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of the intergranular cracks, initiating from the bottom of a pit.
29
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
ML00169 — Drill Pipe Fracture in the Pipe BodyM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - External Surface
Drill Pipe Fracture in the Pipe Body
2
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
Drill Pipe Fracture in the Pipe Body
3
VIEW
ML00169 / Nov.2020
Drill Pipe Fracture in the Pipe Body
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Internal Surface
ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Micrography, as polished, of the hot cracks with rounded morphology.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrographic detail, as polished, of the hot cracks with rounded interdenritic morphology.
26
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Hot cracking
Micrography in low magnification, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
24
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Micrography, as polished, of the crack in the valve thickness, showing the straight aspect of the fatigue propagation.
22
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack
Micrographic detail of the straight crack that propagated by a fatigue mechanism.
18
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - As polished micrographyDf - Fatigue Crack

+2 more from this case →

ML00142 — Impact of a .308 Winchester on AR500 PlateM - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography of the plate section, as polished, close to the surface that suffered the impact. At this magnification it is possible to see a deposit over the plate surface, but no evidences of damage in the plate.
25
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The deposits at the surface are the melted bullet films.
23
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The orange is the copper alloy melted film.
20
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The lead alloy melted and formed this gray deposit.
19
VIEW
ML00142 / Aug.2018
Impact of a .308 Winchester on AR500 Plate
M - Low Alloy Wear ResistantP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - As polished micrographyDf - At the Surface
ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrographic detail of the branch cracking parallel to the fracture, as polished, showing that the cracks are filled with zinc.
61
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Secondary Cracks
Micrographic detail of the branch cracking parallel to the fracture, as polished, showing that the cracks are filled with zinc.
47
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - As polished micrographyDf - Zn Layer
ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
As polished micrographical detail of the cracks at the bottom of the thread fillet. There are several small cracks some of them associated to longitudinal inclusions. There are some regions presenting small "pores".
40
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Crack
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
38
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Crack
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
37
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Secondary Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
33
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks

+3 more from this case →

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the zinc flakes coating layer in the "as polished" condition of a longitudinal section of the bolt.
71
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrography of the longitudinal section of the bolt, at the fracture (top of the figure), starting from the bottom of the thread (to the left side of the figure). The presence of the coating at the bolt surface shows that the fracture occurred without corrosion. The rusted aspect of the fracture is associated to corrosion products after the rupture has occurred, also suggesting that the bolts were fractured and remained in service for some time after the failure occurred.
65
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Fracture