Sampling and Analysis

1 case · 16 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Dendritic Standard: EN AC AlSi7Mg0,3 clear all

Sampling and Analysis — sub-branches

At the Surface 1Base Metal 4Fusion Line 1General View 1Heat Affected Zone 2Transverse Section 2Weld Metal 2Weld Repair 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the wheel. See the schematic drawing in the next figure
467
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Schematic drawing presenting the position in the rim where the repair by welding was conducted. The region was machined after the welding.
77
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Weld Repair
Profile of the rim of the wheel, total width 215 mm. See the schematic drawing in the next figure.
64
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Transverse Section AspectDf - Transverse Section
Schematic drawing indicating the location of the repair by welding
60
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Identification drawingDf - Transverse Section
Detail of the welded region in the rim of the light alloy wheel.
126
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - At the Surface
Micrography of the cast rim, base metal, in the as polished condition, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that sugegsts a solution annealed treatment.
120
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by OMDf - Base Metal

+10 more from this case →