Sampling and Analysis

2 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Duplex Ferritic Austenitic Standard: S32760 Capture method: Optical Microscope clear all

Sampling and Analysis — sub-branches

Heat Affected Zone 4Longitudinal Section 2Transverse Section 2Welded Joint 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of the valve at the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
48
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Welded Joint
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
74
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section

More from these cases

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Micrography of the valve at the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
46
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrographic detail of the fusion line of the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
39
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the valve at the welded joint of the body to the insert (fillet weld). The heat affected zone shows that the sigma phase was removed, which means that the base metal was degradated and during welding the thermal cycle created a condition to remove the sigma phase (dissolve it).
38
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrographic detail of the heat affected zone of the valve to the insert joint showing that the sigma phase was removed, which means that the base metal was degradated and during welding the thermal cycle created a condition to dissolve the sigma phase.
39
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of a transverse section of the forged bar in the center of the thickness. Ferrite and austenite. The ferrite amount, measured by metallographic method, manual counting, is 59%.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Transverse Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. The average austenite spacing is 80 microns, a lot larger than the maximum allowed in the specification, of 30 microns. No detrimental phases were identified at the ferrite/austenite interfaces, but the ferrite phase presented a rough aspect. Higher magnification analysis would be required to identify precipitation.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section