Macrography of the welded joint between the forging and the pipe, showing it was welded in a narrow gap, indicating by the arrow the location of the crack at the margin of the weld, in the forging side.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
Macrography of a section longitudinal to the pipe and transverse to the weld. The thickness of the pipe is 12,7 mm (1/2") and it was welded in 6 passes, the root pass, one fill pass and four cap passes.
855
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - NItal Etched MacroDf - Welded Joint
Micrography of the seam welded joint, autogenous. The localized dissolution occurrs exactly at the weld metal that presents a bainitic structure and Vickers (100g) microhardness values about 230HV, compared to the heat affected zone presenting average of 202 HV and the base metal presenting average of 180HV.
59
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Nital Etched Micrography by SEMDf - Welded Joint
Aspect of the valve body after cutting a slice containg the crack and the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint.
56
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
The 6 1/2" nominal diameter longitudinal seam welded pipe is internally cladded with Alloy 625. The pipe was manufactured by forming a cladded plate (probably welded by rolling) and welding it longitudinally. The pipe was heat treated (quenched and tempered) after the seam weld.
97
VIEW
ML00133 / May.2018
Seam Welded Pipe Cladded with Alloy 625
M - LAS / Ni AlloyP - Longitudinal Seam Welded PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
The 4 1/2" nominal diameter seamless pipe internally overlaid with Alloy 625. This pipe corresponds to a 90° curve. The overlaid pipe was heat treated before and after bending. The final quenching and tempering heat treatment was conducted to meet API 5L X70 properties.
113
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Aspect Before AnalysisDf - Welded Joint
Macrography of a longitudinal section of a 4 mm diameter wire, presenting part of an austogenously welded joint, with the transformation of the strain hardened pearlitic. The base metal is to the left side of the figure, and the heat affected zone is in the center of the figure. There is a (previous austenite) grain growth to the right side of the figure, where it is the center of the weld.
33
VIEW
ML00113 / Jan.2018
Autogenous Weld of a Carbon Steel Wire
M - Medium Carbon SteelP - WireAp - OffshoreCd - Welding
Cm - NItal Etched MacroDf - Welded Joint

More from these cases

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Schematic drawing of the API 5L X52 pipe, butt welded to another pipe, showing the 4 cap passes. The pipe is nominal diameter 8" and thickness 1/2". The qualification of the WPS was conducted according to the structural code, with toughness requirements (Charpy V at 0°C), with 4 lateral bending tests, all approved, and 2 welded joint tensile tests, one with ruptured in the base metal and the other ruptured in the weld metal, both presenting strenght level higher than the minimum specified. The pipe was tensile tested.
95
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Identification drawingDf - Welded Joint
Micrography of the weded joint at the cap pass fusion line. The columnar structure of the weld metal is to the top of the figure; and it is possible to see the coarse grains at the heat affected zone. Both columnar structure and coarse grains are related to the previous austenite grain boundaries. From the fusion line to the base metal (in the bottom of the figure) the grain sizes are refined.
86
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography of the weld metal in the region of the cap pass that was not reheated, last bead, presenting previous austenite columnar grains, coarse.
69
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
Micrography of the weld metal in the root, reheated by the fill pass, presenting a refined ferritic structure.
49
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Welded Joint
ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Macrographic detail of the valve at the welded joint of the SDSS body (left side of the figure) to the Alloy 625 insert (right side of the figure), by a fillet weld. The cracking was arrested at the position of this welded joint.
49
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Low magnification micrography of the valve at the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint because the structures of the weld metal, insert and heat affected zones are tough (austenitic in the weld metal and insert, and free from sigma in the HAZ) .
48
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MicroDf - Welded Joint