Weld Metal

3 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Testpiece for Qualification clear all

Weld Metal — sub-branches

Weld Metal 8Weld Metal in the Cap 2Weld Metal in the Center 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal in the last bead, presenting previous austenite columnar grains, primary ferrite in the grain boundaries, some regions of ferrite with aligned second phases and acicular ferrite.
58
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by SEMDf - Weld Metal
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
96
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal showing a dendritic microstructure. Chromic acid, electrolytic etched.
26
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Weld Metal in the Center

More from these cases

ML00153 — X52 in a Tubular StructureM - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Micrography of the weld metal in the root, reheated by the fill pass, presenting a refined ferritic structure and some islands of second phases, probably agglomerated carbides.
46
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the face of the joint. It is possible to see the columnar grains of acicular ferritic structure. The hardness level of this region varied a little. From 231HV10 at the root until 250HV10 close to the face.
50
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the face of the joint showing the acicular ferrite structure with some regions where the grains started recristalization.
48
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the root of the joint. It is possible to see only reheated regions of primary ferritic structure. The average hardness level of this region is 231HV10.
34
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrography of the weld metal at the root of the joint showing the equiaxial ferritic structure.
33
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
ML00066 — GMAW Welded Joint in 9%Ni Alloy SteelM - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Micrography of the weld metal close to the center. Celular and colunar dendritic structures are visible with a lower magnification. Chromic acid, electrolytic etched.
23
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Weld Metal in the Center
Micrography of the weld metal in the cap pass. Chromic acid, electrolytic etched.
25
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Weld Metal in the Cap
Micrographic detail of the weld metal in the cap pass, presenting a columnar dendritic microstructure. Chromic acid, electrolytic etched.
28
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - Eletrolytically Etched Micrography by OMDf - Weld Metal in the Cap