Weld Metal

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Duplex Ferritic Austenitic clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the weld metal of the pipe to the fitting. It is possible to see columnar grains and recristalized grains. In the same way, the yellow/white is the austenite and the blue/red is the ferite.
67
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrography at the center of the weld metal.
41
VIEW
ML00100 / Nov.2017
Superduplex Tubing to Forging Welded Joint
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Welding
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Micrography of the weld metal of the pipe to the fitting.
63
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Micrographic detail of the weld metal of the pipe to the fitting. Yellow/white austenite and red/blue ferrite (delta).
59
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal
Cap pass in the weld metal, presenting a large amount of delta ferrite (retained) due to a probable quick cool of the pool during welding (since this pass is too thin, perhaps a remelting). Although it is not good to present this microstructure, it did not affect the failure.
54
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Weld Metal