Close to the Internal Surface

1 case · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Brittle Behavior clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
The fracture surface of the casting cylinder presented, at the internal surface, interconnected graphite flakes and a corroded matrix.
73
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the Internal Surface
Micrography of the longitudinal section of the cylinder, at the internal diameter (left side of the figure), in contact with the treated cooling water, presenting large graphite flakes in a predominatly perlitic matrix.
50
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrography of the corroded surface of the cast cylinder, with 0.5 mm penetrations, showing that the graphites are interconnected and create a notch morphology, critical for a material that presents 1% ductility.
31
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic aspect of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
23
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrographic detail of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see a thick oxide layer at the internal surface, characteristic of 10 years operating with treated water, and the large graphite flakes interconnecting.
23
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface

+1 more from this case →