Multiple cracks

6 cases · 15 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Aspect of the clamp surface showing several parallel cracks, transverse to the wire surface, with a brittle aspect.
42
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Multiple cracks
Macrography of the transverse section of the tube, in a position where the cracking was not yet through wall. The internal tube surface shows multiple corrosion fatigue cracks, parallel, under the weld of the membrane, probably related to the cold side of the tube (the cracks opened to the boiler outside). The external side of the tube presenting a small crack at the margem of the weld, suggesting also the action of thermal stresses.
214
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Multiple cracks
Microscopic detail of the cracks at the surface of the pin, close to the fracture. It is possible to see that the cracks are not associated to plastic deformation at the surface. Instead they are brittle and associated to regions where the material lost the passivation (dark grey stains at the surface). Some cracks that already opened (a little) showed deformation at the tips.
1024
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing multiple cracks, typical of a corrosion fatigue mechanism.
861
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Multiple cracks
Macrographic detail of the longitudinal section of the stub end, showing the external side to the top and the internal side to the bottom. There are multiple cracks starting from the external side.
54
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Longitudinal Section AspectDf - Multiple cracks
Macrography of one wire that was fully cracked, in a longitudial section. The morphology shows multiple corrosion-fatigue cracking.
62
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Multiple cracks

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Detail by scanning electron microscop of the clamp surface showing several cracks, parallel. In this image the cracks appear horizontal, but the photo was taken with the axis of the clamp in the vertical direction which means that the cracks are transverse to the axis.
41
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Detailed aspect of the previous figure showing the parallel cracks, transverse to the axis.
37
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrography presenting the internal tube surface, with parallel cracks growthing from pits.
96
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Multiple cracks
ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Low magnification microscopy (stereoscope) detail of the multiple cracks at the pin surface.
146
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - Multiple cracks
Aspect of the pin surface, presenting multiple cracks, paralel to the fracture position.
122
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Multiple cracks
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
51
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
As polished micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing corrosion fatigue cracks. These are multiple cracks, paralel to the main fracture, slightly branched and fully filled with oxides.
43
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - As polished micrographyDf - Multiple cracks
Micrography of the external surface of the tubular equipment, close to the fracture position (it is to the top of the figure), showing multiple cracks, typical of a corrosion fatigue mechanism.
47
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Multiple cracks
ML00168 — SCC of Austenitic SS Flange Stub EndM - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Micrography of the stub end longitudinal section, presenting multiple cracks, branched.
40
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - As polished micrographyDf - Multiple cracks