Microstructure

3 cases · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas Condition: Brittle Behavior clear all

Microstructure — sub-branches

Decarburized Surface 1Martensite 14

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of spring surface, showing the pits full of corrosion deposits and a small decarburized layer (probably from the manufacturing processes).
30
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Decarburized Surface
Micrography of a longitudinal section of the socket at the position where the fracture occurred. Uniform tempered martensitic structure. The hardness of this microstructure is 639 HV1Kg.
74
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a dendritic path of a quenched and tempered martensitic microstructure. The segregated regions (white interdendritic regions) are more clearly identified in low magnification. Voids are located in these segregated regions.
21
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite

More from these cases

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Micrographic detail of the transverse section of the spring wire, martensitic.
24
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the martensitic structure, uniform through thickness.
17
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the martensitic structure, clearly obtained from a refined previous austenitic structure .
19
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by SEMDf - Martensite
Micrographic detail of the martensitic structure.
19
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by SEMDf - Martensite
ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Micrography of a longitudinal section presenting an uniform tempered martensitic structure.
81
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensitic structure.
80
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Brittle Fracture of a High Strength Socket
4
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions.
20
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions. At this magnification the segregation is not clear.
16
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. The hardness level of the material is about 39 HRc.
14
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a region where there is a large amount of casting defects. Shrinkage voids in interdendritic spaces, some interconnected and cracked.
13
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a region where there is a large amount of casting defects. Shrinkage voids in interdendritic spaces, some interconnected and cracked.
13
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite