Longitudinal Section

6 cases · 10 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Metallographic image of a longitudinal section of the clamp (axis in the vertical direction), showing a refined ferritic perlitic structure.
34
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The longitudinal section of the 1/2" thick pipe close to the washout position shows that the external tool marks are like notches that are corroded and cracks are iniciating from the corroded regions. The top of the figure presents the external pipe surface and the bottom of the figure presents the internal pipe surface, with a green coating and the rusted washout.
154
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Longitudinal Section
The stub end was manufactured from a plate and the microstructure in a longitudial section shows a refined granular austenitic structure.
62
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Macrography of the longitudinal section of a fractured bolt, still threaded to the nut and with the lock washer. The cracks can be seen in several positions: in the threads (removing then); in the center of the bolt (branched) and also in the washer (longitudinal branched cracks).
65
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
Micrography of a wire in a longitudinal section, presenting a predominantly oearlitic structure, highly strained. The wires did not present any coating.
104
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
58
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
The clamp presented several cracks, parallel, transverse to the axis. The appearance of the cracks in the metallographic section shows that some cracks propagate and growth with a irregular path.
24
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00168 — SCC of Austenitic SS Flange Stub EndM - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Macrography of the longitudinal section of the stub end, showing the external side to the top and the internal side to the bottom. The stub end was manufactured by welding, longitudinal seam (not evidenced in this image) and circunferential weld of tube to disc (partial penetration). The cracks starts from the external side of the stub end.
31
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Longitudinal Section
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Failure of a Prestressed Concrete Steel Strand
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Longitudinal Section
ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section