General View

6 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Used clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Tin Bronze Wear Ring of Seawater Pump
2
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - General View
The coasters present a handmake look. The grooves are of different sizes and the octogonal shape is irregular. The pieces presented a weight that suggested that the bright finish is a metallic coating, later identified by EDS analysis as silver coating, typical of a decorative plating.
452
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Aspect Before AnalysisDf - General View
The shaft was removed from service without a failure. It was 4' long and the diameters varied from 2 1/2" to 4 1/2". It was analyzed to be specified for purchasing a new one but properties evidenced bad ductility and brittle behavior even at ambient temperature, associated to a microestruture "as hot rolled".
1238
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Aspect of the serrated walrus tool, interchangeable, that was removed at the end of its life. Dimensions of 1" thick, 2" width, 3" long.
419
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Bimetallic engine bearing, removed from service at the end of its life.
356
VIEW
ML00083 / Oct.2017
Steel Back of a Bimetallic Engine Bearing
M - Low Carbon SteelP - Cold FormedAp - ShipCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Aspect of the wheel. See the schematic drawing in the next figure
467
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Tin Bronze Wear Ring of Seawater Pump
2
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - General View
ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Piece that was analysed by non destructive tests. Octogonal shape. Two irregular grooves. The coaster was manufactured in a cooper alloy substrate and a metallic coating. The analysis to reveal the substrate microstructure was conducted on the back of the part, in a non destructive preparation, that included light grinding, polishing and etching.
61
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Aspect Before AnalysisDf - General View
Light grinding the back of the coaster. The surface was only partially ground, removing the metallic coating, and exposing the substrate, that appeared yellow indicating the manufacturing in a cooper alloy.
63
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Preparation TechniqueDf - General View
Back of the coaster showing the region that was prepared for the non destructive analysis. It was ground and polished (the coating was removed), showing the yellow aspect of the substrate, in the left bottom part of the image.
64
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polishedDf - General View
Image presenting the back of the coaster where the microstructure of the substrate was identified. The composition of the brass (about 35% Zn) indicates that the expected structure is alpha plus beta. The front of the coaster presents two grooves which surface morphology was analyzed by scanning electron microscopy.
65
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface AspectDf - General View