Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Valve Body Standard: AISI clear all

Damage — sub-branches

Corrosion 1Crack 6Fatigue Crack 10Localized Corrosion 2Microcracks 2Pitting 1

Results

SortNewestOldestTitle A-ZTitle Z-A
General view of the cylindrical valve body, 6 5/8" nominal diameter, showing a transverse straight crack at the external surface.
406
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Aspect Before AnalysisDf - Crack
The as polished micrographic aspect of the corroded surface shows pitting and several microcracks, probably associated to the biological attack and material embrittlement. Replication technique.
924
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - As polishedDf - Microcracks

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Penetrant test (dye check) image of the cracks at the surface of the actuator hole, viewed from inside of the body after the longitudinal cut. The aspect of the cracks at the hole, close to the internal side of the valve, is not the same as the aspect of the cracks at the external side (a straigth line), suggesting that the original cracks had propagated by fatigue through wall. The penetrant did not stained too much at the cracked area, indicating that the cracks are not too deep in this position, or are not fully opened to the surface.
62
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Aspect by NDTDf - Crack
Magnetic particle test of the same cracks at the edge of the actuator hole, viewed from inside of the body. The cracks appeared more clearly with this test than with the penetrant test, suggesting that the cracks are not fully opened to the surface.
60
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Aspect by NDTDf - Crack
Longitudinal section of the cylindrical body showing two pieces with the cracks, close to the position of the actuator hole. The valve body thickness is 40 mm at the location where the cracks appeared.
53
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Longitudinal Section AspectDf - Crack
Macrography of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. The valve body is 40 mm thick at this position and it is possible to see that at this position only one region is welded in repair, close to the outer surface (top), and there is a crack, transverse to the thickness, that is difficult to see with this magnification and that is clearly the propagation in fatigue.
47
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - Nital Etched Micrography by OMDf - Fatigue Crack
Macrographic detail of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. There is a straight crack, transverse to the thickness that clearly propagated by fatigue mechanism, from the region where the welding defects were created.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack

+10 more from this case →

ML00092 — MIC of a Valve BodyM - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Aspect of the inner side of a valve body, showing regions of localized corrosion and rust, not expected for this stainless steel.
82
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Corrosion
Deep localized corrosion spots, rusted. There are indications that the roughness of the surface influences the localized corrosion location.
61
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Aspect Before AnalysisDf - Localized Corrosion
The macroscopic aspect of the surface after preparation. Grinding and polishing.
50
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Surface AspectDf - Localized Corrosion
The micrographic aspect of the corroded surface, after polishing and etching with Kalling, shows the margin of one pit and microcracks propagating through previous austenite grain boundaries of the martensitic structure, probably associated to the biological attack and material embrittlement. Replication technique.
42
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Kalling etched, OMDf - Pitting
Micrographic details of microcracks propagating through previous austenite grain boundaries of the martensitic structure. Replication technique.
41
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Kalling etched, OMDf - Microcracks