Damage

3 cases · 57 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Alpha & Beta clear all

Damage — sub-branches

Casting defects 1Corrosion 5Crack 1Cracks 1Dezincification 7Dimples 1Ductile Crack 13Melted film 11Plastic Deformation 12Preferential Dissolution 2Secondary Cracks 2Voids 1

Results

SortNewestOldestTitle A-ZTitle Z-A
There are some regions in the coaster surface where pores associated to shrinkage is evident.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - Casting defects
Aspect of the surface of the plate by scanning electron microscopy, at the impact position, showing that the bullet was melted and deposited. The plate presented round cracks in the margin of the projectile impact position.
14
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Aspect of the CuZn platesheet where it is corroded (cooling medium side). The (hot) air cooler uses treated seawater as the cooling medium and the corroded regions are associated to the regions in the heat exchanger of higher temperatures, and the leakage occurred in regions of contact of the platesheet to cooper alloy tubes.
1167
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Corrosion

More from these cases

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Same region of the previous image but is a higher magnification, showing the metallographic aspect of the polished surface of the (back of the) coaster. Shrinkage with a dendritic morphology typical of a casting structure.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Voids
ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Aspect of the surface of the plate, by scanning electron microscopy, in the center of the projectile impact position, showing the melted bullet covering the surface.
14
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Detailed aspect of the surface of the plate at the projectile impact position.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface AspectDf - Melted film
Detailed aspect of the surface of the plate at the projectile impact position.
12
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Aspect of the surface of the plate, by scanning electron microscopy, out of the center of the projectile impact position, showing that the melted bullet covered a large part of the surface.
12
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film
Detailed aspect of the surface of the plate, out of the center of the projectile impact position, showing that the melted bullet covered a large part of the surface.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Surface Aspect by SEMDf - Melted film

+33 more from this case →

ML00125 — Dezincification of a Cooler TubesheetM - BrassP - PlateAp - ShipCd - Preferential Dissolution
Aspect of the tubesheet after removal of the cooper alloy tubes and water cleaning. The corrosion is more intense in the regions of tube connection.
176
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Surface AspectDf - Corrosion
Transverse section of the tubesheet, after removal of the tubes. The seawater sie is to the top of the figure. It is possible to see regions of localized corrosion close to the tube position and a red layer all through the plate surface.
182
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Corrosion
Macrographic detail of the transverse section of the tubesheet at the cooper alloy tube position, after removal of the 5/8" tube. The red layer at the top of the plate (exposed to the cooling medium - treated seawater) is a region of selective corrosion, dezincification.
169
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Corrosion
Macrographic detail of the transverse section of the tubesheet at the cooper alloy tube position, after removal of the 5/8" tube. The "layer" at the top of the plate (exposed to the cooling medium - treated seawater) is a region of selective corrosion, dezincification. It is possible to see that in the right side of the figure, where the cooper tube was positioned, the corrosion damage is deeper.
153
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Transverse Section AspectDf - Dezincification
Micrography of the transverse section of the platesheet at the interface between the corroded and the non-corroded regions. The micrography is in the as polished condition.
140
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Preferential Dissolution

+10 more from this case →