Damage

66 cases · 126 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Aspect Before Analysis clear all

Damage — sub-branches

Brittle Fracture 12Corrosion 17Crack 4Cracking 11Cracks 4Ductile Fracture 1Fatigue Crack 1Fatigue Fracture 5Fracture 41Lap 2Layer Detachment 3Leakage 4Localized Corrosion 5Localized Thinning 1Metal to Metal Wear 2Multiple cracks 2Pitting 1Plastic Deformation 1Secondary Cracks 2Surface Deposits 2Through Wall Cracking 4Washout 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The austenitic stainless steel fitting was removed from the valve body and presented the sdhesion of oily deposits.
150
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - Surface Deposits
Detail of the fracture in the WHEEL 1, changing direction of propagation.
71
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Fracture
Detail of the flat fracture from the notch at the bottom of the recess. No plastic deformation.
113
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Wear of a Carburized Hypoid Gear
1
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - Aspect Before AnalysisDf - Cracks
Detail of the through wall cracking that caused the leakage in the 2" pipe. The crack was originated in the fillet weld, from the end of the reinforced rib.
72
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fatigue Crack
The rotor blade failed without deformation. At the rotor surface it is possible to see different colours of deposits.
53
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
Detail of the cracks associated to deformed regions in the outer wire of a strand.
40
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - Cracks
The small wedge sample is 4 mm deep in the thickness and the circumferential weld are is about 15 mm width where it appears in the internal side of the carcass. The image shows the crack surface (fracture) where the weld aspect is evident.
32
VIEW
ML00174 / Jul.2021
Carburization of a 347 SS Welded Joint
M - Austenitic Stainless SteelP - Fabrication WeldAp - EnergyCd - Carburization
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Detail of the crack in the WHEEL 2, changing direction of propagation exactly like the other whel.
66
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Aspect Before AnalysisDf - Cracking
ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Flat fracture, no plastic deformation, at the notch in the recess.
63
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Brittle Fracture
Brittle Fracture of a LAS Fixing Rod
2
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Brittle Fracture of a LAS Fixing Rod
5
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Brittle Fracture of a LAS Fixing Rod
0
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Detail of the end of the rib, with a crack in the fillet weld metal, propagating through the pipe wall.
40
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Cracking
ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Detail of the fracture surface, dark in the root of the blade, presenting a brittle aspect and indication that it started from this position.
39
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
View of the shaft inserted in the rotor body, and deposits of different colours.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Surface Deposits
View of the rotor body smashed in the internal shaft, the fracture and deposits of different colours. The fracture presented a dark aspect where the failure has started.
18
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Aspect Before AnalysisDf - Fracture
ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
One disassembled wire, 3.2mm diameter, from a strand. The wire presents strong plastic deformation. In a very localized area.
29
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - Plastic Deformation