Damage

2 cases · 29 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure Microstructure: Deformed Structure Capture method: Optical Microscope clear all

Damage — sub-branches

Ductile Crack 9Melted film 4Plastic Deformation 15Secondary Cracks 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the plate section, close to the surface that suffered the impact. The projectile melted and created a film at the surface. HF+HNO3+H2O chemical etch.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Melted film
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The copper alloy melted and created a yellow-orange deposit.
25
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - As polished micrographyDf - Melted film

More from these cases

ML00144 — Impact of a .380 Winchester on Ti64 PlateM - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The projectile sheared the plate but did not perforate it, and the projectile materials (Cu and Pb) deposited at the .surface. HF+HNO3+H2O chemical etch.
9
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The projectile, impacted in the right side of the crack, sheared the plate but did not perforate it and created several longitudinal ductile secondary cracks. HF+HNO3+H2O chemical etch.
16
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrographic detail of the damaged plate (the side of the bullet impact is to the top of the figure). The projectile, in the right side, sheared the plate but did not perforate it and created longitudinal ductile secondary cracks in the middle of the thickness. HF+HNO3+H2O chemical etch.
11
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Secondary Cracks
Micrographic detail of the shearing of the material due to the projectile impact. It is a very localized effect. HF+HNO3+H2O chemical etch.
13
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack
Micrography of the 3/8" thickness titanium alloy plate, in a section. The impact side of the plate is to the top of the figure. The plate was sheared through wall in a very localized position. HF+HNO3+H2O chemical etch.
6
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by OMDf - Ductile Crack

+6 more from this case →

ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Micrographic detail of the plate section, as polished, close to the surface that suffered the impact. The copper alloy melted and created a yellow-orange deposit.
26
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - As polished micrographyDf - Melted film
Micrography of the plate section, close to the surface that suffered the impact. The copper alloy melted and created a yellow-orange deposit. The plate material presented a strong plastic deformation, aligning the grains and strain hardening the microstructure.
26
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Plastic Deformation
Micrographic detail of the copper alloy melted and adhered at the surface and a strong plastic deformation of the plate microstructure.
28
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Plastic Deformation
Micrography of the damaged plate at the side of the bullet impact, top of the figure. The perforated hole expulsed the material to the top and bottom directions and the copper alloy is evident at the hole surface.After etching it is clear the strong plastic deformation of the plate microstructure.
26
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Plastic Deformation
Micrographic detail of the damaged plate at the side of the bullet impact. The perforated hole expulsed the material to the top and bottom directions and the copper alloy is evident at the hole surface. There is a strong plastic deformation of the ferritic-pearlitic microstructure and the hardness level increased from 151 HV to 308 HV (1kg).
20
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - Nital Etched Micrography by OMDf - Plastic Deformation

+11 more from this case →