Damage

5 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: ASTM Capture method: Optical Microscope Detail focus: Longitudinal Section clear all

Damage — sub-branches

Brittle Behavior 6Corrosion 13Ductile Behavior 2Fabrication Defect 12Fatigue 8High Temperature 6Hydrogen 4Repair Defect 1Shooting Effect 1Wear 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of a strain hardened pearlitic structure, in a longitudinal section, of one 3.2mm round wire of one strand.
62
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure. There are vertical "lines" that correspond to segregation bands due to the forming direction. These bands are evident only using low magnification microscopy.
168
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
The fracture of the bolt occurred associated to the bottom of the thread. Compare this photo with the previous one to understand where the fracture started.
115
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. Coarse structure.
61
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section
Micrography of the longitudinal section of the fitiing, in a free-cutting steel. The microstructure is predominantly ferritic and there is a large amount of sulfide inclusions, aligned perpendicular to the forming direction.
98
VIEW
ML00103 / Nov.2017
Brittle Fracture of a Free-Cutting Connector
M - Low Carbon SteelP - Machined PartAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Low magnification micrography of a strain hardened pearlitic structure, in a longitudinal section, of the 1.6mm round wire in the core.
34
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt and a mark at the thread flank that was probably created during tightening of the bolt.
95
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the bolt, close to the fracture surface (top of the figure), The fracture started at the surface (left side) in a position close to the bolt body to bolt head transition.
58
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Longitudinal Section
Micrography of a longitudinal section, in the center of a non-broken bolt that operated in the same assembling, presenting an aged martensitic structure, similar to the broken bolt.
41
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the non-broken 5/8" bolt, at the transition between the threaded body and the head, showing a variation in the grain size (of the previous austenite) and evidences of a deformed structure at this transition.
41
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
ML00123 — Non Qualified Superduplex for SubseaM - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Micrography of a longitudinal section of the forged bar in the center of the thickness. Ferrite and austenite. The average austenite spacing is 80 microns, a lot larger than the maximum allowed in the specification, of 30 microns. No detrimental phases were identified at the ferrite/austenite interfaces, but the ferrite phase presented a rough aspect. Higher magnification analysis would be required to identify precipitation.
53
VIEW
ML00123 / Feb.2018
Non Qualified Superduplex for Subsea
M - Super Duplex Stainless SteelP - BarAp - Oil and GasCd - Not according to spec
Cm - NaOH Electrolytic Etched MicroDf - Longitudinal Section