Damage

15 cases · 23 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: A Capture method: NItal Etched Macro clear all

Damage — sub-branches

Brittle Behavior 6Corrosion 11Ductile Behavior 1Fabrication Defect 12Fatigue 7High Temperature 6Hydrogen 1Repair Defect 1Shooting Effect 1Wear 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the welded joint between the forging and the pipe, showing it was welded in a narrow gap, indicating by the arrow the location of the crack at the margin of the weld, in the forging side.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the longitudinally seam weld of the 24" diameter tube, showing that it was welded from both sides and there is a segregation line in the center of the tube thickness.
737
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Seam
Macrography of a transverse section of the 8" pipe, cut exactly in the middle of the lateral 2" branch line, showing the through thickness crack initiated at the margin of the weld, in the upper part of the pipe.
64
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the 3/8" thickness low carbon steel plate, in a section. The side of bullet impact is to the top of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is larger in the exit of the bullet (to the bottom of the figure).
31
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - NItal Etched MacroDf - Transverse Section
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture
Macrography of a section transverse to the fracture, at the surface of the casting. It is possible to see the large thickness of the galvanized layer at the surface (left side of the figure). There is a white layer over the fracture surface (top of the figure) and branch cracks starting from the surface, parallel to the fracture (in the bottom left side of the figure).
68
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
Macrography of a stud longitudinal sectiion at the fracture position (top of the figure). It is possible to see a large secondary crack at the bottom of the thread fillet adjacent to the fracture surface, without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
56
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
The macrography of a longitudinal section shows that the tube did not present local thinning in any region, but the internal and external scales are evidenced. The external surface (OD) is to the top of the figure and the internal surface (ID) is to the bottom of the figure.
124
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00177 — Cr-Mo Seam Welded TubeM - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Identification of the regions of metallographies of the base metal, heat affected zone (HAZ) and weld metal. Locations in the root, in the center of the thickness and close to the tube OD (external surface).
118
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - NItal Etched MacroDf - Welded Joint
ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Macrography of the 8" pipe, welded to a 2" fitting (weldolet), welded to a 2" flange. The branch line was operating in this position (horizontal line with a lateral branch) and the through thickness fatigue crack is associated to the margin of the weld in the upper part of the pipe.
50
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Cracking
Macrography of a section tranverse to the pipe and to the weld between the 8"pipe and the 2" fitting weldolet. The crack starts exactly at the margin of the weld, in a geometric stress concentration raiser, in a position where it growths in the pipe longitudinal direction, and propagates in a straight line, not related to any metallurgical aspect.
41
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Margin of the Weld Crack
Macrography of a section tranverse to the pipe and to the weld between the 8"pipe and the 2" fitting weldolet. The crack starts exactly at the margin of the weld, in a geometric stress concentration raiser, in a position where it growths in the pipe longitudinal direction, and propagates in a straight line, not related to any metallurgical aspect.
33
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Fatigue Crack
ML00143 — Impact of a .308 Winchester on A36 PlateM - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Macrographic detail of the 3/8" thickness low carbon steel plate. The side of bullet exit is to the bottom of the figure. The perforated hole expulsed the material to the top and bottom directions. The hole is in the right side of the figure.
12
VIEW
ML00143 / Aug.2018
Impact of a .308 Winchester on A36 Plate
M - Low Carbon SteelP - Rolled PlateAp - StructureCd - Pierced
Cm - NItal Etched MacroDf - Transverse Section
ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Macrographic detail of the branch cracks starting from the surface, parallel to the fracture.
64
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks