Damage

2 cases · 3 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Forging Capture method: NaOH Electrolytic Etched Macro clear all

Damage — sub-branches

Brittle Behavior 1Corrosion 3Fabrication Defect 2Hydrogen 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the valve body after cutting a slice containg the crack and the welded joint of the body to the insert (fillet weld). The cracking was arrested at the position of this welded joint.
56
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint
Macrography of a longitudinal section of the flange to pipe weld, cracked in the flange. Pipe thickness, measured, is 5 mm. Flange thickness at the welded region is 7.5 mm. The macro was etched using NaOH solution, electrolytic.
181
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - NaOH Electrolytic Etched MacroDf - Longitudinal Section

More from these cases

ML00134 — Brittle Fracture of a Superduplex Valve BodyM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Macrographic detail of the valve at the welded joint of the SDSS body (left side of the figure) to the Alloy 625 insert (right side of the figure), by a fillet weld. The cracking was arrested at the position of this welded joint.
49
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - NaOH Electrolytic Etched MacroDf - Welded Joint