Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Engine Detail focus: Sampling and Analysis clear all

Damage — sub-branches

Brittle Behavior 1Fabrication Defect 1Fatigue 1High Temperature 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of a flared tubing, cold deformed at 37°, and the circumferential cracking.
483
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
Shaft pinion presenting the bearing surface, with machining markes, from where the thermal spray layer was detached. The diameter of the 880 mm long shaft in this region is about 75 mm.
426
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00167 — Fatigue of a Flared Tubing ConnectionM - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Same flared tubing, with a circumferential crack, with the focus at the internal side.
65
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - General View
Micrography of a longitudinal section of the tubing showing a granular structure, austenitic.
52
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Fracture surface of the tubing, close to the outer diameter.
47
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Close to the External Surface
Micrography of a longitudinal section of the tubing where the fracture occurred. the left side is the outer diameter and the right side is the inner diameter.
37
VIEW
ML00167 / Aug.2020
Fatigue of a Flared Tubing Connection
M - Austenitic Stainless SteelP - TubingAp - EngineCd - Mechanical Fatigue
Cm - Oxalic Acid Electrolytic EtchDf - At the Surface
ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the internal surface (left side). It is possible to see large graphite flakes.
98
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the Internal Surface
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), in the center of the thickness. It is possible to see a mixture of large graphite flakes and rosette grouping flakes.
80
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - In the Center of the Thickness
Micrographic aspect, as polished, of the cast cylinder section at the fracture position (top of the figure), close to the external surface (left side). It is possible to see smaller graphite flakes, interdendritic .
79
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - As polished micrographyDf - Close to the External Surface
The fracture surface of the casting cylinder presented, at the internal surface, interconnected graphite flakes and a corroded matrix.
73
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - Close to the Internal Surface
The fracture surface of the casting cylinder presented, in the center of the thickness, cleavage facets and graphite decohesion that corresponds to a brittle fracture of the material.
61
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fractography by SEMDf - In the Center of the Thickness

+16 more from this case →

ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Macrographic detail of the thermal spray layer in a position of the shaft where it was not detached. Longitudinal section of the shaft. The waves are the machining marks created to anchor the thermal spray layer, that is about 1.5mm thick.
41
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - NItal Etched MacroDf - Longitudinal Section
Shaft microstructure in the longitudinal section, showing aligned segregations typical of the material forming.
31
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Longitudinal Section