Hydrogen

12 cases · 120 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS Capture method: Optical Microscope clear all

Hydrogen — sub-branches

Hydride Formation 2Hydrogen Embrittlement 10

Results

SortNewestOldestTitle A-ZTitle Z-A
In a cut perpendicular to the macroscopic secondary crack it is possible to see several brittle microcracks (branched), indicating that an embrittlement has occurred.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - As polished micrographyDf - Brittle Cracks
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure. There are vertical "lines" that correspond to segregation bands due to the forming direction. These bands are evident only using low magnification microscopy.
168
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Longitudinal section micrography in a position of the thread, far from the failure. The stud presented a quenching and tempering structure and the thread was machined.
84
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Micrography of the longitudinal section of the stud presenting a tempered martensite structure, slightly banded. Hardness 45 HRc.
33
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the bolt showing a martensitic structure, with segregation bands evidenced by the chemical etch.
99
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of the longitudinal section of the link, presenting secondary cracks in the longitudinal direction, following segregation bands in the material.
541
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Micrography of the longitudinal section of the forging material, presenting a granular austenite, precipitation hardened.
84
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the bolt, as polished, presenting brittle cracks, transverse to the bolt axis.
1241
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Cracks

More from these cases

ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The main crack is to the top and the blade surface is to the right, in this micrography that does not reveal any plastic deformation, with transgranular and integranular cracks.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Brittle Fracture
Transgranular and integranular cracks in the alpha matrix full of acicular hydrides .
17
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Hydride Formation
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section, in the center, of the broken 5/8" bolt, presenting an aged martensitic structure.
133
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensitic structure. The bolt presented variations in the previous austenite grain boundaries from the center of the thickness to the surface. No delta ferrite or retained austenite islands are evidenced.
107
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt and a mark at the thread flank that was probably created during tightening of the bolt.
95
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the 5/8" bolt, at the bottom of the thread, presenting a refined structure compared to the center of the bolt. The structure is aged martensite.
91
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the aged martensite structure, refined when compared to the structure in the center of the bolt.
87
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite

+19 more from this case →

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Microstructure of the stud in the longitudinal section, presenting segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration.
69
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Microstructure of the stud in the longitudinal section, out of a region of segregation, where the tempered martensitic microstructure appears more uniform.
72
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the segregated bands, not uniformly distributed in the section. The bands are associated to elongated and aligned inclusions, and a refined microstructure, probably due to carbon and alloying elements concentration. The localized microhardness (50g) in the band showed levels about 540HV, and out of the band, in the same localtion, presented an average hardness of 321 HV, indicating that the material is non uniform in the regions where there are bands.
66
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrographic detail of the martensitic structure of the stud in the longitudinal section, out of a region of segregation, where the microstructure appears more uniform and the microhardness is about 370HV (50g).
62
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Low magnification micrography of a stud longitudinal section in the first thread fillet adjacent to the fracture, presenting a large secondary crack without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+17 more from this case →

ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the stud presenting a tempered martensite structure in the center of the thickness.
33
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Low magnification micrographic image of the stud thread, in the longitudinal section, showing the segregation lines of the steel cut at the thread indicating it was machined.
30
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Micrographic detail of the stud at the thread bottom.
27
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Micrographic detail of the thread top, showing that the thread was machined.
29
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Machined Thread
Micrography of the longitudinal section of the stud showing internal cracks, secondary (not the cracks that opened the fracture). It is evident that the cracking from the thread fillet, of a ductile aspect, presented a different aspect than the internal cracks, of a brittle aspect.
31
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks

+4 more from this case →

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, showing the uniform martensitic structure, not strain hardened.
90
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrography of the longitudinal section of the bolt at the top of the thread fillet, showing a small circunferential cracking typically of a rolling process to manufacture the thread. The thread presented no evidences of plastic deformation suggesting that the heat treatment was applied later. It is important to mention that this cracking presented no influence in the fracture of the bolt.
101
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Rolled Thread
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, in the "as polished" condition, showing the zinc flakes coating layer, applied by a painting process that do not create metallurgical bonding with the substrate.
82
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrographic detail of the zinc flakes coating layer in the "as polished" condition of a longitudinal section of the bolt.
71
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Coating Layer
Micrography of the longitudinal section of the bolt in the center of the thickness (ND 5/8") showing a uniform martensitic structure.
67
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite

+5 more from this case →

ML00079 — Hydrogen Cracking of a Maritime Chain LinkM - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Micrographic detail of the longitudinal section of the link, presenting internal cracks of intergranular morphology, typical of a hydrogen assisted mechanism.
52
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrography of a longitudinal section of the link, presenting a tempered martensitic structure, typical of a quenching and tempering heat treatment and compatible with the link hardness of 43 HRc.
67
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the link, close to the fracture surface (in the top of the figure). There are secondary cracks parallel to the fracture.
33
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of the longitudinal section of the link, close to the fracture surface, presenting the intergranular morphology of the secondary cracks, parallel to the fracture.
29
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of the intergranular secondary cracks, parallel to the fracture, typical of a hydrogen assisted cracking.
29
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
ML00078 — Hydrogen Cracking of IN 718 Subsea ConnectorM - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Micrography of the longitudinal section of the conector, at the fracture position, showing secondary cracks from the fracture surface.
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Fracture
The micrographic detail of the longitudinal section at the fracture surface shows intergranular morphology for the secondary cracks (longitudinal to the forging axis).
64
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
48
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Secondary Cracks
ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Multiple intergranular cracks transverse to the bolt axis. Hydrogen assisted cracking due to cathodic protection of a high strenght steel. Micrography in the "as polished" condition.
104
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Brittle Cracks
Micrography of a longitudinal section of the bolt, as polished, presenting brittle Intergranular and transgranular cracks, transverse to the bolt axis.
94
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Micrography by OMDf - Longitudinal Section
Micrography of a longitudinal section of the bolt, showing the (secondary) crack propagating, transverse to the bolt, from a thread fillet.
91
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the (secondary) crack propagating transverse to the bolt, from a thread fillet.
91
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the (secondary) crack propagating transverse to the bolt, from a thread fillet.
80
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

+5 more from this case →