Brittle Behavior

2 cases · 13 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry Capture method: Scanning Electron Microscope clear all

Brittle Behavior — sub-branches

Brittle Fracture 1Liquid Metal Embrittlement 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic image of the actual rod rupture, showing that the material fractured by an intergranular micromechanism, evidencing a tempered martensite embrittlement.
59
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Fractography by SEMDf - Intergranular Fracture
Micrography of the casting at the surface, presenting a zinc layer deposited in a hot dip process. The thickness of the layer is about 0.3mm in this position, that is higher than expected for this process. The steel substrate is not revealed because the etch was light and the zinc layer protects the low aloy steel during the etch.
93
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by SEMDf - Zn Layer

More from these cases

ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Fractographic detail of the intergranular micromechanism, evidencing a tempered martensite embrittlement.
49
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Fractography by SEMDf - Intergranular Fracture
Fractographic detail of the intergranular micromechanism, evidencing a tempered martensite embrittlement.
44
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Fractography by SEMDf - Intergranular Fracture
Broken tensile testpiece fractography showing predominantly dimples as the fracture micromechanism, and some integranular aspects. It shows that in this uniaxial and without stress concentration raisers, the material presented a ductile behavior.
30
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Fractography by SEMDf - Broken Testpiece
Broken Charpy V testpiece fractography showing intergranular fracture micromechanism. It reveals the brittle material behavior when under critical conditions, like the one that was present in the service application (with a triaxial condition in the notch).
26
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Fractography by SEMDf - Broken Testpiece
ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Scanning electron fractography in low magnification (originally 15x), showing the flat fracture surface with steps and secondary cracks.
72
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
Scanning electron fractography (originally 500x), showing zinc deposits at the fracture surface.
73
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Zn Layer
Scanning electron fractography (originally 1000x), showing details of the zinc deposits at the fracture surface.
72
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Fracture
Scanning electron fractography (originally 500x), showing intergranular aspects in the fracture surface.
43
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture
Scanning electron fractography (originally 1000x), showing intergranular aspects in the fracture surface.
42
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking

+2 more from this case →