Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Secondary Cracks clear all

Scanning Electron Microscope — sub-branches

Fractography by SEM 5Micrography by SEM 1Surface Aspect by SEM 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractography showing brittle secondaryy cracks in the region where the cracking was originated.
34
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fractography by SEMDf - Secondary Cracks
At the surface of the blade there are microcracks with a brittle aspect.
23
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Surface Aspect by SEMDf - Secondary Cracks
Micrographic detail by scanning electron microscopy of the longitudinal ductile secondary cracks. HF+HNO3+H2O chemical etch.
9
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Micrography by SEMDf - Secondary Cracks
Fractographic detail by scanning electron microscopy of the secondary cracks with intergranular morphology.
47
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks
Fractographic detail of the secondary microcracks associated to the sigma phase.
48
VIEW
ML00134 / Aug.2020
Brittle Fracture of a Superduplex Valve Body
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Fracture
Cm - Fractography by SEMDf - Secondary Cracks
Transgranular brittle aspect of the stud fracture surface. Evidences of hydrogen embrittlement.
965
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks

More from these cases

ML00075 — Hydrogen Cracking of IN 718 Subsea FastenersM - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
The fracture of the stud presented transgranular aspects and secondary cracks that appear to be related to small broken particles.
32
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks